Global EPP PA 6C WFN Cast Polyamide 6 + Wax

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Cast
Manufacturer Global EPP
Trade Name PA
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Global EPP PA 6C WFN Cast Polyamide 6 + Wax.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of cast nylons may be altered to suit specific applications, and the performance of the basic polymer can be enhanced with the addition of various additives, fillers, lubricants and colorants.Key characteristics:Unequalled formulation options and profile rangeExcellent mechanical, thermal and chemical resistanceExcellent PV and load bearing capabilitiesExcellent wear and abrasion resistanceGood dimensional stability, largely free from internal stressesFDA compliant grades availableThis supreme abrasion resistant grade contains a blended wax lubrication system, uniformly distributed to radically improve wear resistance and coefficient of friction characteristics. The material has excellent mechanical, thermal and electrical properties and exhibits outstanding pressure velocity capabilities. WFN is particular suited to dry running bearing applications.
Physical Properties Metric English Comments
Density 1.145 g/cc
0.04137 lb/in³
Test Method A; ISO 1183:1987
Water Absorption 0.30 %

@Temperature 23.0 °C,
Time 86400 sec
0.30 %

@Temperature 73.4 °F,
Time 24.0 hour
Immersion; ISO 62:1999 (modified)
Water Absorption at Saturation 5.3 %
5.3 %
ISO 62:1999
Mechanical Properties Metric English Comments
Hardness, Shore D 84
84
ISO 868:2003
Tensile Strength at Break 80.0 MPa
11600 psi
Sample Type 1B, 50mm/min; ISO 527-1/2:1993
Elongation at Break >= 20 %
>= 20 %
Sample Type 1B, 50 mm/min; ISO 527-1/2:1993
Modulus of Elasticity 4.00 GPa
580 ksi
Sample Type 1B, 50 mm/min; ISO 527-1/2:1993
Flexural Strength 105 MPa
15200 psi
1.5 mm/min; ISO 178:2001
Flexural Modulus 3.20 GPa
464 ksi
1.5 mm/min; ISO 178:2001
Compressive Strength 95.0 MPa
13800 psi
Sample Type B, 5 mm/min; ISO 604:2002
Compressive Modulus 2.60 GPa
377 ksi
Sample Type A, 1 mm/min; ISO 604:2002
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
Sample Type A; ISO 180:2000
Coefficient of Friction, Dynamic 0.10

@Pressure 1.75 MPa
0.10

@Pressure 254 psi
31.4 m/min
K (wear) Factor 70.0 x 10-8 mm³/N-M

@Pressure 1.75 MPa
34.7 x 10-10 in³-min/ft-lb-hr

@Pressure 254 psi
31.4 m/min
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-2:1999
Melting Point 220 °C
428 °F
Maximum Service Temperature, Air 110 °C
230 °F
Continuous
180 °C
356 °F
Intermittent
Minimum Service Temperature, Air -100 °C
-148 °F
Intermittent
-40.0 °C
-40.0 °F
Continuous
Flammability, UL94 HB
HB
IEC 60695-11-10:2003-08
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093:1980-01
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093:1980-01
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
3.7

@Frequency 1.00e+6 Hz
IEC 60250:1969-01
4.0

@Frequency 100 Hz
4.0

@Frequency 100 Hz
IEC 60250:1969-01
Dielectric Strength 25.0 kV/mm
635 kV/in
IEC 60243-1:1998-01
Comparative Tracking Index 600 V
600 V
IEC 60112:2003-01
Descriptive Properties Value Comments
Color Red and Grey