Gharda Chemicals G-PAEK™ 1230GF Ultra High Performance PEK Polymer

Category	Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Glass Fiber Filled
Manufacturer	Gharda Chemicals
Trade Name	G-PAEK™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Gharda Chemicals G-PAEK™ 1230GF Ultra High Performance PEK Polymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Details: Ultra High Performance Thermoplastic material, 30% glass fiber reinforced in Poly Aryl Ether Ketone, semi-crystalline granules suitable for injection molding, standard flow, Beige in colorApplication Areas: Suitable for high temperature application, where higher strength needed in load-bearing application. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.

Physical Properties	Metric	English	Comments
Specific Gravity	1.50 g/cc	1.50 g/cc
Water Absorption	0.050 % @Time 86400 sec	0.050 % @Time 24.0 hour
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	410°C nozzle, 220°C mold
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	410°C nozzle, 220°C mold
Crystallinity	40 %	40 %	DSC

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	105	105	ASTM D785
Hardness, Shore D	90	90
Tensile Strength at Break	50.0 MPa @Temperature 250 °C	7250 psi @Temperature 482 °F	ASTM D638
	65.0 MPa @Temperature 200 °C	9430 psi @Temperature 392 °F	ASTM D638
	100 MPa @Temperature 150 °C	14500 psi @Temperature 302 °F	ASTM D638
	135 MPa @Temperature 100 °C	19600 psi @Temperature 212 °F	ASTM D638
	185 MPa @Temperature 23.0 °C	26800 psi @Temperature 73.4 °F	ASTM D638
	190 MPa @Temperature -10.0 °C	27600 psi @Temperature 14.0 °F	ASTM D638
	205 MPa @Temperature -50.0 °C	29700 psi @Temperature -58.0 °F	ASTM D638
Elongation at Break	2.0 - 3.0 %	2.0 - 3.0 %	ASTM D638
Tensile Modulus	11.5 GPa	1670 ksi	ASTM D638
Flexural Strength	280 MPa	40600 psi	ASTM D790
Flexural Modulus	10.5 GPa	1520 ksi	ASTM D790
Izod Impact, Notched	0.600 J/cm	1.12 ft-lb/in	ASTM D256
Izod Impact, Unnotched	6.10 J/cm	11.4 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	370 - 372 °C	698 - 702 °F	DSC
Deflection Temperature at 1.8 MPa (264 psi)	360 °C	680 °F
Glass Transition Temp, Tg	152 - 154 °C	306 - 309 °F	DSC/onset
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Surface Resistivity per Square	1.00e+16 ohm	1.00e+16 ohm	ASTM D257
Dielectric Strength	14.0 kV/mm @Thickness 3.20 mm	356 kV/in @Thickness 0.126 in	ASTM D149
Arc Resistance	160 sec	160 sec	at 500 Volts; ASTM D495
Comparative Tracking Index	140 V	140 V	per 50 drops; ASTM D3638

Processing Properties	Metric	English
Processing Temperature	390 - 425 °C	734 - 797 °F
Nozzle Temperature	425 °C	797 °F
Mold Temperature	200 - 220 °C	392 - 428 °F
Drying Temperature	150 °C	302 °F
Dry Time	4 - 6 hour	4 - 6 hour

Descriptive Properties	Value	Comments
Hopper/ Throat Temperature	60-80°C