Fujipoly Industries Sarcon® GR-Hb Gap Filler Pad

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® GR-Hb Gap Filler Pad.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon GR-b is a highly conformable, thermally conductive material in areas where space between surfaces is uneven and surface textures vary.Information provided by Fujipoly Industries
Physical Properties Metric English Comments
Specific Gravity 2.50 g/cc
2.50 g/cc
150°C for 1,000 hrs; JIS-K-6220
2.50 g/cc
2.50 g/cc
JIS-K-6220; ASTM D-792
2.50 g/cc
2.50 g/cc
70°C for 1,000 hrs; JIS-K-6220
2.50 g/cc
2.50 g/cc
150°C for 1,000 hrs with 90% RH; JIS-K-6220
Mechanical Properties Metric English Comments
Hardness, Shore C 20
20
60°C for 1,000 hrs with 90% RH; SRIS0101
24
24
70°C for 1,000 hrs; SRIS0101
29
29
150°C for 1,000 hrs; SRIS0101
Hardness, Shore OO 49
49
SRIS0101; ASTM D-2240
Tensile Strength, Yield 0.100 MPa
14.5 psi
JIS-K-6251(#2)/ASTM D-412
0.300 MPa
43.5 psi
150°C for 1,000 hrs; JIS-K-6251(#2)
0.300 MPa
43.5 psi
60°C for 1,000 hrs with 90% RH; JIS-K-6251(#2)
0.400 MPa
58.0 psi
70°C for 1,000 hrs; JIS-K-6251(#2)
Elongation at Yield 50 %
50 %
150°C for 1,000 hrs; JIS-K-6251(#2)
60 %
60 %
70°C for 1,000 hrs; JIS-K-6251(#2)
70 %
70 %
60°C for 1,000 hrs with 90% RH; JIS-K-6251(#2)
80 %
80 %
JIS-K-6251(#2)/ASTM D-412
Tear Strength 1.00 kN/m
5.71 pli
150°C for 1,000 hrs; JIS-K-6252 (Angle)
1.00 kN/m
5.71 pli
60°C for 1,000 hrs with 90% RH; JIS-K-6252 (Angle)
1.00 kN/m
5.71 pli
70°C for 1,000 hrs; JIS-K-6252 (Angle)
1.00 kN/m
5.71 pli
JIS-K-6252 (Angle)/ASTM D-624
Thermal Properties Metric English Comments
Thermal Conductivity 2.30 W/m-K
16.0 BTU-in/hr-ft²-°F
JIS-R-2618; ASTM D2326
2.30 W/m-K
16.0 BTU-in/hr-ft²-°F
150°C for 1,000 hrs; JIS-R-2618
2.30 W/m-K
16.0 BTU-in/hr-ft²-°F
60°C for 1,000 hrs with 90% RH; JIS-R-2618
2.30 W/m-K
16.0 BTU-in/hr-ft²-°F
70°C for 1,000 hrs; JIS-R-2618; ASTM D2326
Maximum Service Temperature, Air 200 °C
392 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+13 ohm-cm
2.00e+13 ohm-cm
60°C for 500 hrs with 90% RH; JIS-K-6249
1.00e+14 ohm-cm
1.00e+14 ohm-cm
JIS-K-6249/ASTM D257
2.20e+14 ohm-cm
2.20e+14 ohm-cm
150°C for 1,000 hrs; JIS-K-6249
3.30e+14 ohm-cm
3.30e+14 ohm-cm
70°C for 1,000 hrs; JIS-K-6249
Dielectric Strength 11.0 kV/mm
279 kV/in
JIS-K-6249; ASTM D-149
19.0 kV/mm
483 kV/in
70°C for 1,000 hrs; JIS-K-6249
20.0 kV/mm
508 kV/in
60°C for 1,000 hrs with 90% RH; JIS-K-6249
22.0 kV/mm
559 kV/in
150°C for 1,000 hrs; JIS-K-6249
Dielectric Breakdown 8000 V
8000 V
Withstand Voltage [V/min]; JIS-K-6249; ASTM D-149
Descriptive Properties Value Comments
Color Gray