Fujipoly Industries Sarcon® 45H Thin-Film HR

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® 45H Thin-Film HR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon HR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GHR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 85
85
ASTM D2240
89
89
60°C for 500 hrs; ASTM D2240
95
95
150°C for 1,000 hrs; ASTM D2240
99
99
200°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 5.111 MPa
741.3 psi
6.22 MPa
902 psi
150°C for 1,000 hrs
6.89 MPa
999 psi
200°C for 1,000 hrs
Elongation at Yield 25 %
25 %
200°C for 1,000 hrs
30 %
30 %
150°C for 1,000 hrs
60 %
60 %
Tear Strength 0.300 kN/m
1.71 pli
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 2.40e+13 ohm-cm
2.40e+13 ohm-cm
60°C for 500 hrs
1.00e+15 ohm-cm
1.00e+15 ohm-cm
4.70e+15 ohm-cm
4.70e+15 ohm-cm
150°C for 1,000 hrs
5.60e+15 ohm-cm
5.60e+15 ohm-cm
200°C for 1,000 hrs
Dielectric Constant 4.3

@Frequency 50 Hz
 4.3

@Frequency 50 Hz
 After 1000 hrs at 200°C
4.3

@Frequency 1e+6 Hz
 4.3

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
4.3

@Frequency 1000 Hz
 4.3

@Frequency 1000 Hz
 After 1000 hrs at 200°C
4.5

@Frequency 1e+6 Hz
 4.5

@Frequency 1e+6 Hz
4.5

@Frequency 1000 Hz
 4.5

@Frequency 1000 Hz
4.6

@Frequency 1000 Hz
 4.6

@Frequency 1000 Hz
 After 1000 hrs at 150°C
4.6

@Frequency 50 Hz
 4.6

@Frequency 50 Hz
4.6

@Frequency 50 Hz
 4.6

@Frequency 50 Hz
 After 1000 hrs at 150°C
4.6

@Frequency 1e+6 Hz
 4.6

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
5.1

@Frequency 1e+6 Hz
 5.1

@Frequency 1e+6 Hz
 After 500 hrs at 60°C
5.3

@Frequency 1000 Hz
 5.3

@Frequency 1000 Hz
 After 500 hrs at 60°C
5.5

@Frequency 50 Hz
 5.5

@Frequency 50 Hz
 After 500 hrs at 60°C
Dielectric Strength 5.00 kV/mm
127 kV/in
60°C for 500 hrs
6.00 kV/mm
152 kV/in
200°C for 1,000 hrs
8.10 kV/mm
206 kV/in
AC 60 Hz; 150°C for 1,000 hrs
10.0 kV/mm
254 kV/in
AC 60 Hz
Dielectric Breakdown 7000 V
7000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.0030

@Frequency 50 Hz
 0.0030

@Frequency 50 Hz
 After 1000 hrs at 150°C
0.0030

@Frequency 1000 Hz
 0.0030

@Frequency 1000 Hz
 After 1000 hrs at 150°C
0.0030

@Frequency 50 Hz
 0.0030

@Frequency 50 Hz
 After 1000 hrs at 200°C
0.0030

@Frequency 1000 Hz
 0.0030

@Frequency 1000 Hz
 After 1000 hrs at 200°C
0.0030

@Frequency 1e+6 Hz
 0.0030

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
0.0030

@Frequency 1e+6 Hz
 0.0030

@Frequency 1e+6 Hz
0.0040

@Frequency 1000 Hz
 0.0040

@Frequency 1000 Hz
0.0040

@Frequency 1e+6 Hz
 0.0040

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
0.0070

@Frequency 1e+6 Hz
 0.0070

@Frequency 1e+6 Hz
 After 500 hrs at 60°C
0.0070

@Frequency 50 Hz
 0.0070

@Frequency 50 Hz
0.014

@Frequency 1000 Hz
 0.014

@Frequency 1000 Hz
 After 500 hrs at 60°C
0.024

@Frequency 50 Hz
 0.024

@Frequency 50 Hz
 After 500 hrs at 60°C
Descriptive Properties Value Comments
Color Brown
Thermal Impedance 0.52°C/W
FTM P-3010; ASTM D5470