Fujipoly Industries Sarcon® 45GSR Thin-Film GSR

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® 45GSR Thin-Film GSR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon GSR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GSR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 85
85
ASTM D2240
90
90
150°C for 1,000 hrs; ASTM D2240
91
91
60°C for 500 hrs with 95% RH; ASTM D2240
Tensile Strength, Yield 31.11 MPa
4512 psi
150°C for 1,000 hrs; ASTM D1458
40.0 MPa
5800 psi
60°C for 500 hrs with 95% RH
40.0 MPa
5800 psi
Elongation at Yield <= 3.0 %
<= 3.0 %
<= 3.0 %
<= 3.0 %
150°C for 1,000 hrs; ASTM D1458
<= 3.0 %
<= 3.0 %
60°C for 500 hrs with 95% RH; ASTM D1458
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 9.00e+14 ohm-cm
9.00e+14 ohm-cm
60°C for 500 hrs with 95% RH
1.00e+15 ohm-cm
1.00e+15 ohm-cm
1.50e+15 ohm-cm
1.50e+15 ohm-cm
150°C for 1,000 hrs
Dielectric Constant 3.09

@Frequency 50 Hz
3.09

@Frequency 50 Hz
After 1000 hrs at 150°C
3.09

@Frequency 1000 Hz
3.09

@Frequency 1000 Hz
After 1000 hrs at 150°C
3.11

@Frequency 1e+6 Hz
3.11

@Frequency 1e+6 Hz
After 1000 hrs at 150°C
3.12

@Frequency 1e+6 Hz
3.12

@Frequency 1e+6 Hz
After 500 hrs at 60°C with 95% RH
3.13

@Frequency 1000 Hz
3.13

@Frequency 1000 Hz
After 500 hrs at 60°C with 95% RH
3.15

@Frequency 50 Hz
3.15

@Frequency 50 Hz
After 500 hrs at 60°C with 95% RH
3.2

@Frequency 1000 Hz
3.2

@Frequency 1000 Hz
3.2

@Frequency 1e+6 Hz
3.2

@Frequency 1e+6 Hz
3.2

@Frequency 50 Hz
3.2

@Frequency 50 Hz
Dielectric Strength 15.0 kV/mm
381 kV/in
AC 60 Hz
17.0 kV/mm
432 kV/in
AC 60 Hz
18.0 kV/mm
457 kV/in
AC 60 Hz
Dielectric Breakdown 7000 V
7000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.00010

@Frequency 1000 Hz
0.00010

@Frequency 1000 Hz
0.00020

@Frequency 1e+6 Hz
0.00020

@Frequency 1e+6 Hz
0.00020

@Frequency 1e+6 Hz
0.00020

@Frequency 1e+6 Hz
After 1000 hrs at 150°C
0.00030

@Frequency 1000 Hz
0.00030

@Frequency 1000 Hz
After 1000 hrs at 150°C
0.0011

@Frequency 1e+6 Hz
0.0011

@Frequency 1e+6 Hz
After 500 hrs at 60°C with 95% RH
0.0011

@Frequency 50 Hz
0.0011

@Frequency 50 Hz
After 1000 hrs at 150°C
0.0016

@Frequency 50 Hz
0.0016

@Frequency 50 Hz
0.0024

@Frequency 1000 Hz
0.0024

@Frequency 1000 Hz
After 500 hrs at 60°C with 95% RH
0.0059

@Frequency 50 Hz
0.0059

@Frequency 50 Hz
After 500 hrs at 60°C with 95% RH
Descriptive Properties Value Comments
Color White
Thermal Impedance 0.39°C/W
FTM P-3010; ASTM D5470
Thermal Impedance AD Type 0.71°C/W
FTM P-3010; ASTM D5470