Fujipoly Industries Sarcon® 20GSR Thin-Film GSR

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® 20GSR Thin-Film GSR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon GSR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GSR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 85
85
ASTM D2240
85
85
60°C for 500 hrs with 95% RH; ASTM D2240
88
88
150°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 30.0 MPa
4350 psi
150°C for 1,000 hrs; ASTM D1458
70.0 MPa
10200 psi
80.0 MPa
11600 psi
60°C for 500 hrs with 95% RH
Elongation at Yield <= 3.0 %
<= 3.0 %
<= 3.0 %
<= 3.0 %
150°C for 1,000 hrs; ASTM D1458
<= 3.0 %
<= 3.0 %
60°C for 500 hrs with 95% RH; ASTM D1458
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
2.50e+15 ohm-cm
2.50e+15 ohm-cm
150°C for 1,000 hrs
8.40e+16 ohm-cm
8.40e+16 ohm-cm
60°C for 500 hrs with 95% RH
Dielectric Constant 1.84

@Frequency 1000 Hz
 1.84

@Frequency 1000 Hz
 After 500 hrs at 60°C with 95% RH
1.85

@Frequency 1e+6 Hz
 1.85

@Frequency 1e+6 Hz
 After 500 hrs at 60°C with 95% RH
1.92

@Frequency 50 Hz
 1.92

@Frequency 50 Hz
 After 1000 hrs at 150°C
1.92

@Frequency 1000 Hz
 1.92

@Frequency 1000 Hz
 After 1000 hrs at 150°C
1.93

@Frequency 1e+6 Hz
 1.93

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
2.09

@Frequency 50 Hz
 2.09

@Frequency 50 Hz
 After 500 hrs at 60°C with 95% RH
2.6

@Frequency 1000 Hz
 2.6

@Frequency 1000 Hz
2.6

@Frequency 50 Hz
 2.6

@Frequency 50 Hz
2.6

@Frequency 1e+6 Hz
 2.6

@Frequency 1e+6 Hz
Dielectric Strength 5.00 kV/mm
127 kV/in
AC 60 Hz
6.00 kV/mm
152 kV/in
AC 60 Hz
6.00 kV/mm
152 kV/in
AC 60 Hz
Dielectric Breakdown 3000 V
3000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.00010

@Frequency 1000 Hz
 0.00010

@Frequency 1000 Hz
 After 500 hrs at 60°C with 95% RH
0.00040

@Frequency 1e+6 Hz
 0.00040

@Frequency 1e+6 Hz
 After 500 hrs at 60°C with 95% RH
0.00040

@Frequency 50 Hz
 0.00040

@Frequency 50 Hz
 After 500 hrs at 60°C with 95% RH
0.00040

@Frequency 1e+6 Hz
 0.00040

@Frequency 1e+6 Hz
0.00050

@Frequency 1000 Hz
 0.00050

@Frequency 1000 Hz
 After 1000 hrs at 150°C
0.00060

@Frequency 1e+6 Hz
 0.00060

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
0.00070

@Frequency 1000 Hz
 0.00070

@Frequency 1000 Hz
0.0015

@Frequency 50 Hz
 0.0015

@Frequency 50 Hz
 After 1000 hrs at 150°C
0.0026

@Frequency 50 Hz
 0.0026

@Frequency 50 Hz
Descriptive Properties Value Comments
Color White
Thermal Impedance 0.30°C/W
FTM P-3010; ASTM D5470
Thermal Impedance AD Type 0.64°C/W
FTM P-3010; ASTM D5470