Material Notes:
Sarcon HR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GHR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 92
92
ASTM D2240
92
92
200°C for 1,000 hrs; ASTM D2240
92
92
60°C for 500 hrs; ASTM D2240
93
93
150°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 40.0 MPa
5800 psi
ASTM D1458
42.5 MPa
6160 psi
200°C for 1,000 hrs
48.0 MPa
6960 psi
150°C for 1,000 hrs; ASTM D1458
Elongation at Yield <= 2.0 %
<= 2.0 %
ASTM D1458
<= 2.0 %
<= 2.0 %
150°C for 1,000 hrs; ASTM D1458
<= 2.0 %
<= 2.0 %
200°C for 1,000 hrs; ASTM D1458
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+10 ohm-cm
2.00e+10 ohm-cm
60°C for 500 hrs
1.00e+15 ohm-cm
1.00e+15 ohm-cm
7.30e+15 ohm-cm
7.30e+15 ohm-cm
150°C for 1,000 hrs
1.80e+16 ohm-cm
1.80e+16 ohm-cm
200°C for 1,000 hrs
Dielectric Constant 2.9

@Frequency 50 Hz
 2.9

@Frequency 50 Hz
 After 1000 hrs at 150°C
2.9

@Frequency 50 Hz
 2.9

@Frequency 50 Hz
 After 1000 hrs at 200°C
2.9

@Frequency 1000 Hz
 2.9

@Frequency 1000 Hz
 After 1000 hrs at 150°C
2.9

@Frequency 1000 Hz
 2.9

@Frequency 1000 Hz
 After 1000 hrs at 200°C
2.9

@Frequency 1e+6 Hz
 2.9

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
2.9

@Frequency 1e+6 Hz
 2.9

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
3.3

@Frequency 1e+6 Hz
 3.3

@Frequency 1e+6 Hz
3.3

@Frequency 50 Hz
 3.3

@Frequency 50 Hz
3.3

@Frequency 1000 Hz
 3.3

@Frequency 1000 Hz
4.0

@Frequency 1e+6 Hz
 4.0

@Frequency 1e+6 Hz
 After 500 hrs at 60°C
4.1

@Frequency 1000 Hz
 4.1

@Frequency 1000 Hz
 After 500 hrs at 60°C
4.4

@Frequency 50 Hz
 4.4

@Frequency 50 Hz
 After 500 hrs at 60°C
Dielectric Strength 4.00 kV/mm
102 kV/in
200°C for 1,000 hrs
4.00 kV/mm
102 kV/in
60°C for 500 hrs
5.00 kV/mm
127 kV/in
150°C for 1,000 hrs
6.00 kV/mm
152 kV/in
AC 60 Hz
Dielectric Breakdown 4000 V
4000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.0010

@Frequency 1000 Hz
 0.0010

@Frequency 1000 Hz
 After 1000 hrs at 200°C
0.0020

@Frequency 1000 Hz
 0.0020

@Frequency 1000 Hz
 After 1000 hrs at 150°C
0.0020

@Frequency 50 Hz
 0.0020

@Frequency 50 Hz
 After 1000 hrs at 200°C
0.0030

@Frequency 1e+6 Hz
 0.0030

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
0.0030

@Frequency 1e+6 Hz
 0.0030

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
0.0030

@Frequency 1000 Hz
 0.0030

@Frequency 1000 Hz
0.0040

@Frequency 1e+6 Hz
 0.0040

@Frequency 1e+6 Hz
0.0040

@Frequency 50 Hz
 0.0040

@Frequency 50 Hz
 After 1000 hrs at 150°C
0.0090

@Frequency 50 Hz
 0.0090

@Frequency 50 Hz
0.014

@Frequency 1e+6 Hz
 0.014

@Frequency 1e+6 Hz
 After 500 hrs at 60°C
0.026

@Frequency 1000 Hz
 0.026

@Frequency 1000 Hz
 After 500 hrs at 60°C
0.061

@Frequency 50 Hz
 0.061

@Frequency 50 Hz
 After 500 hrs at 60°C
Descriptive Properties Value Comments
Color Brown
Thermal Impedance 0.57°C/W
FTM P-3010; ASTM D5470
Thermal Impedance AD Type 0.66°C/W
FTM P-3010; ASTM D5470