Fujipoly Industries Sarcon® 15GTR Thin-Film GTR

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® 15GTR Thin-Film GTR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon TR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GTR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 87
87
ASTM D2240
87
87
150°C for 1,000 hrs; ASTM D2240
87
87
60°C for 500 hrs; ASTM D2240
88
88
200°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 44.0 MPa
6380 psi
200°C for 1,000 hrs; ASTM D1458
60.666 MPa
8798.9 psi
150°C for 1,000 hrs
73.3 MPa
10600 psi
Elongation at Yield <= 2.0 %
<= 2.0 %
<= 2.0 %
<= 2.0 %
150°C for 1,000 hrs; ASTM D1458
<= 2.0 %
<= 2.0 %
200°C for 1,000 hrs; ASTM D1458
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 9.10e+13 ohm-cm
9.10e+13 ohm-cm
60°C for 500 hrs
1.00e+15 ohm-cm
1.00e+15 ohm-cm
1.10e+15 ohm-cm
1.10e+15 ohm-cm
200°C for 1,000 hrs
9.10e+15 ohm-cm
9.10e+15 ohm-cm
150°C for 1,000 hrs
Dielectric Constant 2.1

@Frequency 50 Hz
2.1

@Frequency 50 Hz
After 1000 hrs at 200°C
2.1

@Frequency 1000 Hz
2.1

@Frequency 1000 Hz
After 1000 hrs at 200°C
2.1

@Frequency 1e+6 Hz
2.1

@Frequency 1e+6 Hz
After 1000 hrs at 200°C
2.2

@Frequency 1000 Hz
2.2

@Frequency 1000 Hz
After 1000 hrs at 150°C
2.3

@Frequency 50 Hz
2.3

@Frequency 50 Hz
After 1000 hrs at 150°C
2.3

@Frequency 1e+6 Hz
2.3

@Frequency 1e+6 Hz
After 1000 hrs at 150°C
2.7

@Frequency 50 Hz
2.7

@Frequency 50 Hz
After 500 hrs at 60°C
2.7

@Frequency 1e+6 Hz
2.7

@Frequency 1e+6 Hz
After 500 hrs at 60°C
2.7

@Frequency 1000 Hz
2.7

@Frequency 1000 Hz
After 500 hrs at 60°C
Dielectric Strength 3.00 kV/mm
76.2 kV/in
60°C for 500 hrs
3.00 kV/mm
76.2 kV/in
AC 60 Hz; 200°C for 1,000 hrs
3.50 kV/mm
88.9 kV/in
150°C for 1,000 hrs
4.00 kV/mm
102 kV/in
AC 60 Hz
Dielectric Breakdown 4000 V
4000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
After 1000 hrs at 200°C
0.0020

@Frequency 1e+6 Hz
0.0020

@Frequency 1e+6 Hz
After 1000 hrs at 200°C
0.0020

@Frequency 50 Hz
0.0020

@Frequency 50 Hz
After 1000 hrs at 150°C
0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
After 1000 hrs at 150°C
0.0020

@Frequency 1e+6 Hz
0.0020

@Frequency 1e+6 Hz
After 1000 hrs at 150°C
0.0030

@Frequency 50 Hz
0.0030

@Frequency 50 Hz
After 1000 hrs at 200°C
0.0040

@Frequency 1000 Hz
0.0040

@Frequency 1000 Hz
0.0040

@Frequency 1e+6 Hz
0.0040

@Frequency 1e+6 Hz
0.0050

@Frequency 1e+6 Hz
0.0050

@Frequency 1e+6 Hz
After 500 hrs at 60°C
0.0080

@Frequency 50 Hz
0.0080

@Frequency 50 Hz
0.0080

@Frequency 1000 Hz
0.0080

@Frequency 1000 Hz
After 500 hrs at 60°C
0.024

@Frequency 50 Hz
0.024

@Frequency 50 Hz
After 500 hrs at 60°C
Descriptive Properties Value Comments
Color Grey-Green
Thermal Impedance 0.51°C/W
FTM P-3010; ASTM D5470
Thermal Impedance AD Type 0.78°C/W
FTM P-3010; ASTM D5470