Formosa Plastics Formolene® 6145O Impact Copolymer Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer Formosa Plastics Corporation, USA
Trade Name Formolene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Formosa Plastics Formolene® 6145O Impact Copolymer Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Impact Copolymer for Appliance Applications Formolene® 6145O is a medium impact copolymer of polypropylene characterized by its easy mold flow, physical property balance and excellent dimensional stability. It is designed for consumer products and appliance applications requiring long-term heat-aging resistance and flexural endurance. It has additional stiffness for good service performance Formolene® 6145O has earned a UL continuous service rating of 110°C with recognition for typical use in laundry equipment. This material is free of animal-derived content.Specimens were injection molded according to the conditions specified in ASTM D4101Information provided by Formosa Plastics Corporation, USA
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
ASTM D1505
Melt Flow 20 g/10 min

@Temperature 230 °C
20 g/10 min

@Temperature 446 °F
I<sub>2</sub>; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 29.0 MPa
4200 psi
2" (50mm) per min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
2" (50mm) per min; ASTM D638
Flexural Modulus 0.134 GPa
19.4 ksi
1.3mm per min, 1% secant; ASTM D790
Izod Impact, Notched 0.961 J/cm

@Temperature 23.0 °C
1.80 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 106 °C
223 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 59.0 °C
138 °F
ASTM D648