- Polytetrafluoroethylene (PTFE), Carbon Fiber Filled
- Fluorseals PTFE 25% carbon filled
Fluorseals PTFE 25% carbon filled
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Carbon Fiber Filled |
| Manufacturer | Fluorseals |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fluorseals PTFE 25% carbon filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Improved compressive strength, wear resistance and thermal conductivity.Information provided by TEKU GmbH Fluorkunststoffe, a distributor of Fluorseals materials.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.09 g/cc | 0.0755 lb/in³ | ASTM 1457-62 T |
| Deformation | 6.0 % | 6.0 % | 14 MPa, 100 h, 23°C; ASTM D621-59 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 38.0 MPa | 5510 psi | ASTM 1457-62 T |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM 1457-62 T |
| Elongation at Break | 170 % | 170 % | ASTM 1457-62 T |
| Coefficient of Friction, Dynamic | 0.12 - 0.14 | 0.12 - 0.14 | v = 1 m/s |
| 0.12 - 0.15 | 0.12 - 0.15 | v = 1.9 m/s | |
| Abrasion | 0.55 | 0.55 | mm of depth after 200 hrs load duration; Partner Material ST 50 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C @Temperature 100 °C |
55.6 µin/in-°F @Temperature 212 °F |
DIN 52328 |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | DIN 52612 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 ohm-cm | 1000 ohm-cm | DIN 53482 |
| Surface Resistance | 1000 ohm | 1000 ohm | DIN 53482 |
Users viewing this material also viewed the following:
- Polimeri Europa Greenflex® ML 60 Ethylene Vinyl Acetate Copolymer - Injection Molding, Compounding & Extrusion
- Loxim 830 01 HBCC Polypropylene Compound 30% Chemically Coupled, Flame Retardant
- Momentive Performance Materials PolarTherm® PT110 Boron Nitride (BN) Powder
- SABIC Innovative Plastics LNP LUBRICOMP LCL33E PEEK
- SABIC Innovative Plastics LNP Thermocomp TH0450D PUR (Asia Pacific)
- A. Schulman SCHULAMID® 66 PTFE20 HS 20% PTFE Lubricated, Heat Stabilized Nylon 6/6
- ExxonMobil Mobil Delvac 10W-30 1300 Super
- Overview of materials for Epoxy Molding Compound
- SABIC Innovative Plastics LNP LUBRICOMP DL002ER PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved