Fibre Glast 1110 L Vinyl Ester Resin (Laminate Properties)

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Vinyl Ester , Vinyl Ester Sheet Molding Compound
Manufacturer Fibre Glast Developments Corporation
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fibre Glast 1110 L Vinyl Ester Resin (Laminate Properties).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
#1110 is a low viscosity, corrosion resistant vinyl ester resin. It is formulated for maximum corrosion resistance to most fuels, vapors, and both acidic and basic chemicals. It is also heat resistant and blended for toughness. The raw materials used in the manufacture of this resin are listed as acceptable in FDA regulatory Title 21 CFR 177.2420 for repeated use in contact with food subject to compliance with the prescribed limitation of that regulation.Performance:Excellent corrosion resistanceExcellent impact strengthHigh tensile elongationFDA applicationProperties listed typical of 0.125" Laminate thickness, 25% glass, 1 veil, 2 mats. See also: "Vinyl Ester Resin (Casting Properties)" for information on that application.Can be used for hand lay-up and spray-up, filament winding, flake glass and filled lining and coating compounds. Perfect for repairing tank linings, blistering boat hulls, and fabricating tough all-around parts.Information provided by Fibre Glast Developments Corporation.
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0372 lb/in³
Liquid Property
Solids Content 52 %
52 %
Liquid Property
Brookfield Viscosity 275 cP
275 cP
Liquid Property
Mechanical Properties Metric English Comments
Tensile Strength at Break 91.7 MPa
13300 psi
Tensile Modulus 6.83 GPa
990 ksi
Flexural Strength 140 MPa
20300 psi
Flexural Modulus 5.24 GPa
760 ksi
Thermal Properties Metric English Comments
Flash Point 22.8 - 37.8 °C
73.0 - 100 °F
Liquid Property