- FKuR Kunststoff Fibrolon® P 8540 Wood-Plastic Compound, Fiber Reinforced
FKuR Kunststoff Fibrolon® P 8540 Wood-Plastic Compound, Fiber Reinforced
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polypropylene (PP) , Wood and Natural Products |
| Manufacturer | FKuR Kunststoff GmbH |
| Trade Name | Fibrolon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | FKuR Kunststoff Fibrolon® P 8540 Wood-Plastic Compound, Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FIBROLON® are fiber reinforced compounds. Fibrolon® P 8540 has a polypropylene base. With the brand name of FIBROLON® FKuR has developed natural fiber reinforced compounds (Wood-Plastics-Composites: WPC), which, unlike many other WPC, can be injection molded without problems. Furthermore it is possible to process FIBROLON® to complex profiles, panels and hollow profiles and/or into components for the automotive interiors. FIBROLON® compounds are distinguished by high strength and a stiffness comparable to wood.Information Provided by FKuR Kunststoff GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.360 g/cc | 0.0130 lb/in³ | ISO 60 |
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Melt Flow | 2.0 - 3.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
2.0 - 3.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 24.0 MPa | 3480 psi | ISO 527 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ISO 527 |
| Elongation at Break | 4.5 % | 4.5 % | ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 3.40 GPa | 493 ksi | ISO 527 |
| Flexural Yield Strength | 41.0 MPa | 5950 psi | at 3.5% strain; 6% strain at break; ISO 178 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1/1eU |
| Charpy Impact, Notched | 0.360 J/cm² @Temperature 23.0 °C |
1.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 - 180 °C | 320 - 356 °F | ISO 3146-C |
| Vicat Softening Point | 155 °C | 311 °F | A; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Melt Volume Flow (cm3/10 min) | 3-4 | ISO 1133; 190°C, 5kg |
Users viewing this material also viewed the following:
- Rogers Corporation RO4003C Glass-Reinforced Hydrocarbon and Ceramic Laminate with Thin Film Resistor Foil
- PTS Trimid® N6-200L Nylon 6 with Lube
- PolyOne Elastamax™ EG-9090 Thermoplastic Elastomer (TPE)
- PolyOne Geon™ Vinyl Flexible R295AE Polyvinyl Chloride, Flexible (PVC, Flexible)
- Iran Petrochemical (PCC) LL0209AA Linear Low Density Polyethylene
- LyondellBasell Hifaxâ„¢ CB251 Thermoplastic Polyolefin Elastomer
- Tra-Con Tra-Cast 3101 Encapsulating Adhesive System
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR Hi-Sil 233 Filler
- Henkel Fixodine M Surface Conditioner
Copyright © lookpolymers.com All Rights Reserved