ExxonMobil Santoprene® 241-45 Thermoplastic Elastomer  (discontinued **)

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Santoprene® 241-45 Thermoplastic Elastomer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A soft, colorable, specialty thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It complies with NSF 61 for plumbing applications in contact with potable water. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It is polyolefin based and completely recyclable.Complies with NSF Standard 61: Piping System Components for Drinking Water.Recommended for applications requiring excellent flex fatigue resistance.Used in sealing applications.Information provided by Advanced Elastomer Systems
Physical Properties Metric English Comments
Specific Gravity 0.970 g/cc
0.970 g/cc
23°C; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 45
45
.12 in; ASTM D2240
Tensile Strength at Break 3.52 MPa
510 psi
Across Flow; ASTM D412
Tensile Strength, Ultimate 1.24 MPa
180 psi
Across Flow; ASTM D412
Elongation at Break 400 %
400 %
Across Flow; ASTM D412
Compression Set 15 %
15 %
73°F, 22 hr; ASTM D395
50 %
50 %
212°F, 168 hr; ASTM D395
Processing Properties Metric English Comments
Processing Temperature 175 - 230 °C
347 - 446 °F
Rear Barrel Temperature 177 °C
350 °F
Middle Barrel Temperature 182 °C
360 °F
Front Barrel Temperature 182 °C
360 °F
Nozzle Temperature 188 - 221 °C
370 - 430 °F
Die Temperature 199 °C
390 °F
Extrusion
Melt Temperature 196 °C
385 °F
Extrusion
193 - 232 °C
380 - 450 °F
Processing
Mold Temperature 10.0 - 51.7 °C
50.0 - 125 °F
Processing
Drying Temperature 82.2 °C
180 °F
Dry Time 3 hour
3 hour
Moisture Content 0.080 %
0.080 %
Back Pressure 0.345 - 0.689 MPa
50.0 - 100 psi
Processing
5.00 - 20.0 MPa
725 - 2900 psi
Extrusion
Clamp Pressure 41.4 - 68.9 MPa
6000 - 10000 psi
Vent Depth 0.00254 cm
0.00100 in
Cushion 0.317 - 0.635 cm
0.125 - 0.250 in
Screw Speed 100 - 200 rpm
100 - 200 rpm
Descriptive Properties Value Comments
Color Natural Color
Form Pellets
Injection Rate Fast
Maximum Regrind % 20
Screw Compression Ratio 2:1 - 2.5:1
Screw L/D Ratio 16:1 - 20:1
Copyright © lookpolymers.com All Rights Reserved