ExxonMobil Paxon™ BA53-035 Blow Molding Resin  (discontinued **)

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Paxon™ BA53-035 Blow Molding Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BA53-035 is a high molecular weight, high density polyethylene copolymer offering an outstanding combination of stiffness and toughness. The resin provides superior melt strength and impact resistance.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.953 g/cc
0.0344 lb/in³
ASTM D4883
ESCR 100% Igepal® 600 hour
600 hour
ASTM D1693 Condition B
Melt Flow 3.5 g/10 min
3.5 g/10 min
190 / 21.6 (HLMI); ASTM D1238
<= 0.10 g/10 min

@Load 2.16 kg,
Temperature 190 °C
<= 0.10 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 29.0 MPa
4200 psi
ASTM D638
Elongation at Break 1200 %
1200 %
ASTM D638
Flexural Modulus 1.38 GPa
200 ksi
Method1, Procedure A (1"x3"x0.125"), Tangent calculation; ASTM D790
Tensile Impact Strength 567 kJ/m²
270 ft-lb/in²
ASTM D1822
399 kJ/m²

@Temperature -40.0 °C
190 ft-lb/in²

@Temperature -40.0 °F
ASTM D1822
Thermal Properties Metric English Comments
CTE, linear 120 µm/m-°C

@Temperature 20.0 °C
66.7 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 77.0 °C
171 °F
ASTM D648
Vicat Softening Point 127 °C
260 °F
ASTM D1525
Brittleness Temperature <= -76.1 °C
<= -105 °F
ASTM D746
Processing Properties Metric English Comments
Melt Temperature 191 °C
375 °F
Descriptive Properties Value Comments
Features Thermal Stabilizer