ExxonMobil Paxon™ 4700 Blown Film Extrusion Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Paxon™ 4700 Blown Film Extrusion Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
4700 is a medium molecular weight, high density polyethylene homopolymer film resin. It can be processed on conventional film extrusion equipment.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.963 g/cc
0.0348 lb/in³
ASTM D4883
Water Vapor Transmission 11.6 g/m²/day
0.747 g/100 in²/day
ASTM E969
Oxygen Transmission Rate 5580 cc/m²/day
359 cc/100 in²/day
ASTM D1434
Melt Flow 0.73 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.73 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
11 g/10 min

@Load 10.0 kg,
Temperature 190 °C
11 g/10 min

@Load 22.0 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 38.6 MPa
5600 psi
ASTM D882
Film Tensile Strength at Yield, TD 34.5 MPa
5000 psi
ASTM D882
Film Elongation at Break, MD 900 %
900 %
ASTM D882
Film Elongation at Yield, MD 9.0 %
9.0 %
ASTM D882
Elmendorf Tear Strength, MD 0.472 g/micron
12.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 9.84 g/micron
250 g/mil
ASTM D1922
Dart Drop Test 35.0 g
0.0772 lb
ASTM D1709
Film Tensile Strength at Break, MD 37.2 MPa
5400 psi
ASTM D882
Film Tensile Strength at Break, TD 30.3 MPa
4400 psi
ASTM D882
1% Secant Modulus, MD 1030 MPa
150000 psi
ASTM D882
1% Secant Modulus, TD 1140 MPa
165000 psi
ASTM D882
Descriptive Properties Value Comments
Features Thermal Stabilizer