ExxonMobil PP8013L1 Polypropylene Impact Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer Exxon Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil PP8013L1 Polypropylene Impact Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A nucleated impact copolymer resin with very high impact strength at low temperature. It is suitable for molding applications like containers and tubs, other rigid packaging, tools and boxes. It is also suitable as compound base stock applications.Availability: Africa & Middle East and Europe Features:DuctileMedium Flow NucleatedUltra High Impact Resistance Uses: CompoundingConstruction Applications Industrial Applications Rigid Packaging Processing Method: Injection Molding and CompoundingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
ExxonMobil Method
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 58
58
ISO 868
Tensile Strength, Yield 17.0 MPa
2470 psi
ISO 527-2/50
Elongation at Yield 4.0 %
4.0 %
ISO 527-2/50
Tensile Modulus 0.951 GPa
138 ksi
ISO527-2/1
Flexural Modulus 0.903 GPa
131 ksi
ISO 178
Izod Impact, Notched (ISO) 50.4 kJ/m²
24.0 ft-lb/in²
ISO 180/1A
Charpy Impact, Notched 1.01 J/cm²

@Temperature -20.0 °C
4.80 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
1.41 J/cm²

@Temperature 0.000 °C
6.70 ft-lb/in²

@Temperature 32.0 °F
ISO 179/1eA
4.41 J/cm²

@Temperature 22.8 °C
21.0 ft-lb/in²

@Temperature 73.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 325 °C
617 °F
ISO 3146
Crystallization Temperature 256 °C
493 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 75.0 °C
167 °F
ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 46.1 °C
115 °F
ISO 75-2/A
Vicat Softening Point 140 °C
284 °F
ISO 306/A50