ExxonMobil PP7684KN Impact Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer Exxon Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil PP7684KN Impact Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A high crystallinity, high impact copolymer resin with medium melt flow rate and excellent processing attributes. It is designed for injection molded small and large appliance parts.Availability: North America and Asia Pacific Features:Fast Molding CycleGood Heat Aging ResistanceGood ProcessabilityHigh Impact ResistanceHigh StiffnessLow WarpageUses: Appliances Consumer Applications CratesIndustrial ApplicationsPackagingTool/Tote BoxProcessing Method: Injection Molding and CompoundingInformation provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
ASTM D792
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 230 °C
20 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 24.4 MPa
3540 psi
ISO 527-2/50
25.5 MPa
3700 psi
2 in/min; ASTM D638
Elongation at Yield 3.4 %
3.4 %
ISO 527-2/50
5.0 %
5.0 %
ASTM D638
Tensile Modulus 1.32 GPa
191 ksi
ISO 527-2/1
Flexural Modulus 1.28 GPa
185 ksi
1% secant, 0.05 in/min.; ASTM D790
Flexural Modulus, 1% Secant 1290 MPa
187000 psi
ASTM D790A
1480 MPa
214000 psi
ASTM D790B
Izod Impact, Notched 1.66 J/cm
3.10 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 3.99 kJ/m²

@Temperature -40.0 °C
1.90 ft-lb/in²

@Temperature -40.0 °F
ISO 180/1A
4.62 kJ/m²

@Temperature -17.8 °C
2.20 ft-lb/in²

@Temperature 0.000 °F
ISO 180/1A
8.40 kJ/m²

@Temperature 22.8 °C
4.00 ft-lb/in²

@Temperature 73.0 °F
ISO 180/1A
Charpy Impact, Notched 3.99 J/cm²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
ISO 79/1eA
4.83 J/cm²

@Temperature -20.0 °C
23.0 ft-lb/in²

@Temperature -4.00 °F
ISO 79/1eA
6.51 J/cm²

@Temperature 0.000 °C
31.0 ft-lb/in²

@Temperature 32.0 °F
ISO 79/1eA
10.1 J/cm²

@Temperature 22.8 °C
48.1 ft-lb/in²

@Temperature 73.0 °F
ISO 79/1eA
Gardner Impact 19.1 J

@Thickness 3.17 mm,
Temperature -30.0 °C
14.1 ft-lb

@Thickness 0.125 in,
Temperature -22.0 °F
ASTM D5420
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 102 °C
216 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 92.8 °C
199 °F
ISO 75-2/Bf
Processing Properties Metric English Comments
Processing Temperature 204 - 232 °C
399 - 450 °F
Typical