ExxonMobil Optema® TC-114 Blown Ethylene Methyl Acrylate
| Category | Polymer , Film , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Optema® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Optema® TC-114 Blown Ethylene Methyl Acrylate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Optema TC 114 is an ethylene methyl acrylate copolymer specifically formulated to offer extrusion and property performance for blown film applications. It produces a soft, elastic film with good handling characteristics without additional additives. Optema TC 114 can produce film under 1.0 mil thickness. Availability: Latin America, North America and South America Additive: Anitblock: 14000 ppmSlip: 3000 ppmThermal Stabilizer: YesApplications: Disposable GlovesHospital DrapesUpholstery FilmData provided by the manufacturer, Exxon Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | Exxon Method |
| Methyl Acrylate Content | 18 % | 18 % | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 3.20 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Antiblock Level | 14000 ppm | 14000 ppm | |
| Slip Level | 3000 ppm | 3000 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 380 % | 380 % | ASTM D882 |
| Film Elongation at Break, TD | 670 % | 670 % | ASTM D882 |
| Elmendorf Tear Strength MD | 50 g | 50 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 310 g | 310 g | ASTM D1922 |
| Dart Drop Test | 370 g | 0.816 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 20.0 MPa | 2900 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 |
| 1% Secant Modulus, MD | 49.6 MPa | 7200 psi | ASTM D882 |
| 1% Secant Modulus, TD | 51.7 MPa | 7500 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 81.0 °C | 178 °F | Exxon Method |
| Vicat Softening Point | 57.2 °C | 135 °F | ASTM D882 |