ExxonMobil Optema® TC-110 Blown Ethylene Methyl Acrylate

Category Polymer , Film , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Extrusion Grade
Manufacturer Exxon Chemical
Trade Name Optema®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Optema® TC-110 Blown Ethylene Methyl Acrylate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Optema TC 110 is an ethylene methyl acrylate copolymer specifically formulated to offer extrusion and property performance for blown film applications. It produces a soft, elastic film with good handling characteristics without additional additives. It can produce film under 1.0 mil thickness.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: YesApplications: Disposable GlovesHospital DrapesUpholstery FilmData provided by the manufacturer, Exxon Chemical.
Physical Properties Metric English Comments
Density 0.942 g/cc
0.0340 lb/in³
Exxon Method
Methyl Acrylate Content 21.5 %
21.5 %
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 2.00 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.00 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 370 %
370 %
ASTM D882
Film Elongation at Break, TD 650 %
650 %
ASTM D882
Elmendorf Tear Strength MD 30 g
30 g
ASTM D1922
Elmendorf Tear Strength TD 320 g
320 g
ASTM D1922
Dart Drop Test 430 g
0.948 lb
ASTM D1709A
Film Tensile Strength at Break, MD 20.0 MPa
2900 psi
ASTM D882
Film Tensile Strength at Break, TD 20.7 MPa
3000 psi
ASTM D882
1% Secant Modulus, MD 42.7 MPa
6200 psi
ASTM D882
1% Secant Modulus, TD 40.0 MPa
5800 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 176 °C
349 °F
Peak Temperature; Exxon Method
Vicat Softening Point 127 °C
261 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 16 %
16 %
ASTM D1003
Gloss 34 %
34 %
45°; ASTM D2457