ExxonMobil Oppalyte™ 52MHR647 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Oppalyte™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Oppalyte™ 52MHR647 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A super white opaque, modified higher density, biaxially oriented PP film, humidity resistant acrylic coated two sides. This film is designed to wrap products with a high moisture content or products stored in humid conditions. It provides outstanding performance on all packaging machines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Excellent humidity seal retention on both sidesLow sealing thresholdHigh seal strengths even under low pressure sealingGood aroma barrierExcellent packaging machine performanceOutstanding opacity, white background and reduced show-throughExcellent stiffnessIdeal support for normal ink systemsWater based coatingsFeatures:Flavor & Aroma Barrier Humidity ResistantHumidity Resistant Acrylic CoatedLight BarrierApplications:BakeryBox OverwrapFresh ProduceFrozen FoodHealth and Beauty Care Household and Detergents Ice CreamIndustrial Uses:Box Overwrap Flexible PackagingHFFS Flexible Packaging Pre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
Physical Properties Metric English Comments
Oxygen Transmission Rate 650 cc/m²/day

@Temperature 23.0 °C
41.9 cc/100 in²/day

@Temperature 73.4 °F
Wet, 75% RH; ExxonMobil Method
652 cc/m²/day

@Temperature 23.0 °C
42.0 cc/100 in²/day

@Temperature 73.4 °F
0% RH; ExxonMobil Method
Thickness 50.8 microns
2.00 mil
ExxonMobil Method
Coating Weight 37.6 g/m²
23.5 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 170 %
170 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 55 %
55 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 1.70 GPa
247 ksi
MD; ExxonMobil Method
2.80 GPa
406 ksi
TD; ExxonMobil Method
Coefficient of Friction 0.25
0.25
Both Sides; ExxonMobil Method
Film Tensile Strength at Break, MD 105 MPa
15200 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 185 MPa
26800 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 4.0 %

@Temperature 135 °C,
Time 432 sec
4.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 2.0 %

@Temperature 135 °C,
Time 432 sec
2.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Gloss 70 %
70 %
45°; ExxonMobil Method
Transmission, Visible 22 %
22 %
ExxonMobil Method
Descriptive Properties Value Comments
Whiteness Index 90
Yield 18400 in2/lb