ExxonMobil Oppalyte™ 36MO747 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Oppalyte™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Oppalyte™ 36MO747 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A white opaque biaxially oriented polypropylene film acrylic coated on one side, one side PVdC. Provides outstanding performances on all packaging machines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features: Broad sealing range on both sidesExcellent aroma, oxygen and moisture barriersSuperior opacityHigh yieldExcellent stiffnessCoatings are mutually compatible and compatible with converter-applies PVdC coatingExcellent base for converty-applied coatingSolvent-free coatingsIdeal support for water based ink printing Features: Acrylic CoatedFlavor & Aroma BarrierGas BarrierIn Lamination Lap SealableLight BarrierMoisture BarrierOxygen BarrierPVdC coatedSealable PVdC CoatedApplications:BakeryBiscuits/Cookie/Crackers Box OverwrapConfectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Fresh ProduceFrozen FoodHealth and Beauty CareHousehold and DetergentsIce Cream Uses:Box Overwrap Flexible Packaging HFFS Flexible Packaging Pre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 1.10 g/m²/day @Temperature 23.0 °C |
0.0710 g/100 in²/day @Temperature 73.4 °F |
85% RH; ExxonMobil Method |
| 4.81 g/m²/day @Temperature 38.0 °C |
0.310 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method | |
| Oxygen Transmission Rate | 20.0 cc/m²/day @Temperature 23.0 °C |
1.29 cc/100 in²/day @Temperature 73.4 °F |
Wet, 75% RH; ExxonMobil Method |
| 20.2 cc/m²/day @Temperature 23.0 °C |
1.30 cc/100 in²/day @Temperature 73.4 °F |
0% RH; ExxonMobil Method | |
| Thickness | 35.6 microns | 1.40 mil | ExxonMobil Method |
| Coating Weight | 24.3 g/m² | 15.2 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 130 % | 130 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 50 % | 50 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 1.50 GPa | 218 ksi | MD; ExxonMobil Method |
| 2.50 GPa | 363 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.25 | 0.25 | Acrylic; ExxonMobil Method |
| 0.35 | 0.35 | PVdC; ExxonMobil Method | |
| Seal Strength | 360 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C |
360 g/in @Pressure 40.0 psi, Temperature 266 °F |
Otto Brugger, 0.2 sec, PVdC; ExxonMobil Method |
| 360 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C |
360 g/in @Pressure 40.0 psi, Temperature 266 °F |
Otto Brugger, 0.2 sec, Acrylic; ExxonMobil Method | |
| Film Tensile Strength at Break, MD | 115 MPa | 16700 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 170 MPa | 24700 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 6.0 % @Temperature 135 °C, Time 432 sec |
6.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 100 % | 100 % | 45°, PVdC Surface; ExxonMobil Method |
| Transmission, Visible | 22 % | 22 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Carbon Dioxide Transmission Rate | 5.16 cc/100 in2/ 24 hr | 75% RH, ASTM D1434 |
| Heat Seal Range | 54°F | PVdC, 36.3 psi, 0.2 sec |
| 90°F | Acrylic, 36.3 psi, 0.2 sec | |
| Nitrogen Transmission Rate | 0.645 cc/100 in2/ 24 hr | 75% RH, ASTM D1434 |
| Yield | 28400 in2/lb |