ExxonMobil NTX™ NTX 101 Super Strength Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | NTX™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil NTX™ NTX 101 Super Strength Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NTX 101 is a super strength hexene copolymer LLDPE film resin. Films made from this resin have outstanding toughness properties, especially impact and tear strength, compared to other hexene copolymers. It is stabilized for blown film extrusion and does not contain slip or antiblock, making it well suited for blown stretch wrap.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 9.10 MPa | 1320 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.38 MPa | 1360 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 630 % | 630 % | ASTM D882 |
| Film Elongation at Break, TD | 720 % | 720 % | ASTM D882 |
| Puncture Energy | 3.62 J | 2.67 ft-lb | ExxonMobil |
| Elmendorf Tear Strength, MD | 18.1 g/micron | 460 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 23.6 g/micron | 600 g/mil | ASTM D1922 |
| Dart Drop | 13.0 g/micron | 330 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 62.6 MPa | 9080 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 50.8 MPa | 7370 psi | ASTM D882 |
| 1% Secant Modulus, MD | 163 MPa | 23700 psi | ASTM D882 |
| 1% Secant Modulus, TD | 183 MPa | 26500 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 123 °C | 253 °F | Peak Melting Temperature; ExxonMobil Method |
| Crystallization Temperature | 109 °C | 228 °F | ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 17 % | 17 % | ASTM D1003 |
| Gloss | 37 % | 37 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |