Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

ExxonMobil Metallyte™ UHB 35 MWHB OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Metallyte™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Metallyte™ UHB 35 MWHB OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A multi-layer, cavitaed, white OPP film structure that has exceptional barrier to gases and flavors. It is metalized on one side and treated on the other. It is designed for use in laminations or as a converted monoweb, especially with converter-applied cold seal sealants. The treated face has surface sealing characteristics for fine sealing and will lap seal to some coextruded OPP films.Availability: Latin America, North America and South AmericaKey Features:Outstanding opacityOutstanding moisture and oxygen barrierOutstanding aroma and flavor barrierExcellent flex-Crack resistanceExcellent surface for high graphic qualityFeatures:Flavor & Aroma BarrierGas Barrier In Lamination Lap SealableLight BarrierMoisture BarrierOxygen BarrierApplications:Bakery Uses: HFFS Flexible Packaging Pouches – Flexible PackagingPre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Extrusion Coating, Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Solvent Flexographic Priming, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Water Vapor Transmission 0.295 g/m²/day

@Temperature 38.0 °C
0.0190 g/100 in²/day

@Temperature 100 °F
90% RH; ExxonMobil Method
Oxygen Transmission Rate 0.0931 cc/m²/day
0.00600 cc/100 in²/day
ExxonMobil Method
Thickness 35.6 microns
1.40 mil
ExxonMobil Method
Coating Weight 24.8 g/m²
15.5 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Break, MD 75.2 MPa
10900 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 84.8 MPa
12300 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 5.0 %

@Temperature 135 °C
5.0 %

@Temperature 275 °F
ExxonMobil Method
Shrinkage, TD 5.0 %

@Temperature 135 °C
5.0 %

@Temperature 275 °F
ExxonMobil Method
Descriptive Properties Value Comments
Treatment 40 dyne/cm
Treated Surface
Yield 27900 in2/lb
Copyright © lookpolymers.com All Rights Reserved