ExxonMobil Metallyte™ 12MM281 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Metallyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Metallyte™ 12MM281 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A high barrier, non-sealable OPP film with one-side metalized and one-side treated. 12MM281 is designed for use as the center web of a triplex adhesive lamination. The treated surface offers excellent compatibility with laminating adhesives and cohesives (cold seals).Availability: Latin America, North America and South AmericaKey Features:Outstanding light barrierExcellent moisture and oxygen barriersExcellent cold seal adhesionAdhesive lamination capableExcellent metal adhesion and appearanceFeatures: Light BarrierMoisture BarrierOxygen BarrierApplications:BakeryBiscuits/Cookie/CrackersConfectionery, Chocolate Confectionery, Gum Confectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Pet Food Uses: HFFS Flexible Packaging Pouches – Flexible Packaging VFFS Flexible PackagingProcessing Method: Cold Seal Adhesive and Middle Web Adhesive LaminationInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 0.0931 g/m²/day @Temperature 38.0 °C |
0.00600 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method |
| Oxygen Transmission Rate | 18.6 cc/m²/day @Temperature 23.0 °C |
1.20 cc/100 in²/day @Temperature 73.4 °F |
0% RH; ExxonMobil Method |
| Thickness | 12.7 microns | 0.500 mil | ExxonMobil Method |
| Coating Weight | 11.4 g/m² | 7.10 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 262 MPa | 38000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % @Temperature 135 °C |
5.0 % @Temperature 275 °F |
ExxonMobil Method |
| Shrinkage, TD | 5.0 % @Temperature 135 °C |
5.0 % @Temperature 275 °F |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Optical Density | 2.4 | 2.4 | ExxonMobil Method |
| Transmission, Visible | 0.40 % | 0.40 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Wetting Tension | 0.85 receding cos theta | Matte Surface |
| Yield | 61200 in2/lb |