Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

ExxonMobil Label-Lyte™ 28LLG MET OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Label-Lyte™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Label-Lyte™ 28LLG MET OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A clear, one-side metallized, one-side treated oriented polypropylene film. The metalized layer is designed to provide a bright metal appearance in surface print or laminated applications. The treated, satin-white side is designed for machinability and hot melt adhesion. 28 LLG MET is designed for use in roll-fed labeling of cylindrical glass, plastic, and metal containers. Typical applications include food, beverage, nutritional, aerosol, and household chemicals. This film can be used as an inside web in lamination.Availability: Latin America, North America and South AmericaKey Features: Excellent opacity and bright metal background for outstanding graphic appealVery good hot melt adhesionConsistent machinability on roll-fed label machinesFeatures:Two Side ProcessableApplications:Beverage, CarbonatedBeverage, Mineral WatersDairy ProductsDry Foods and Beverage PowdersHealth and Beauty CareHousehold and DetergentsIndustrial Uses: Reel-Fed Labels Processing Method: Inner Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Thickness 27.9 microns
1.10 mil
ExxonMobil Method
Coating Weight 17.3 g/m²
10.8 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 110 %
110 %
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 40 %
40 %
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Coefficient of Friction 0.36
0.36
Adhesive Surface; ExxonMobil Method
0.60
0.60
Print Surface; ExxonMobil Method
Film Tensile Strength at Break, MD 71.7 MPa
10400 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 120 MPa
17400 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 5.0 %

@Temperature 135 °C
5.0 %

@Temperature 275 °F
ExxonMobil Method
Shrinkage, TD 3.0 %

@Temperature 135 °C
3.0 %

@Temperature 275 °F
ExxonMobil Method
Optical Properties Metric English Comments
Optical Density 2.3
2.3
ExxonMobil Method
Descriptive Properties Value Comments
Wetting Tension 0.85 receding cos theta
Print Surface
Yield 40000 in2/lb