ExxonMobil Label-Lyte® 25 LLG-101 Clear OPP Film

Category Polymer , Adhesive , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Label-Lyte®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Label-Lyte® 25 LLG-101 Clear OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A clear, one-side treated, biaxially oriented polypropylene film that is used in roll-fed labeling. This film can be laminated to itself (at other gauges of LLG-101) or applied as outer webs to other films. It is formulated with a proprietary non-migratory slip system. The treated clear layer is the intended print and laminating surface. The machinable high gloss layer is receptive to hot melt adhesive.Availability: Latin America, North America and South AmericaKey Features: Outstanding clarity and glossExcellent ink adhesion with most solvent-based and water-based ink systemsExcellent bond strength with most laminating adhesivesContains non-migratory slip system for outstanding performance on roll-fed labeling machinesGood hot melt adhesionApplications:Beverage, CarbonatedBeverage, Mineral WatersDairy ProductsDry Foods and Beverage Powders Uses: Reel-Fed Labels Processing Method: Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Thickness 25.4 microns
1.00 mil
ExxonMobil Method
Coating Weight 22.7 g/m²
14.2 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 174 %
174 %
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 45 %
45 %
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Coefficient of Friction 0.19
0.19
Machinable; ExxonMobil Method
Film Tensile Strength at Break, MD 124 MPa
18000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 241 MPa
35000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 4.0 %
4.0 %
at 275°F; ExxonMobil Method
Shrinkage, TD 4.0 %
4.0 %
at 275°F; ExxonMobil Method
Optical Properties Metric English Comments
Haze 2.0 %
2.0 %
ExxonMobil Method
Gloss 87 %
87 %
45°, Machinable Surface; ExxonMobil Method
Transmission, Visible 90 %
90 %
clear; thickness not quantified
Descriptive Properties Value Comments
Wetting Tension 0.83 receding COS theta
Print Surface
Yield 30500 in2/lb