- ExxonMobil LLDPE LL 1236.85 Linear Low Density Polyethylene Resin
ExxonMobil LLDPE LL 1236.85 Linear Low Density Polyethylene Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Exxon Chemical |
| Trade Name | LLDPE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LLDPE LL 1236.85 Linear Low Density Polyethylene Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: LL 1236 Series resins are butane LLDPEs with increased stiffness and a high melt index. They can be used alone or as a component in packaging and industrial film, blown or cast. Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: 400 ppmProcessing Aid: Yes Thermal Stabilizer: YesApplications: Blown FilmBread BagsCast FilmFood packagingPackaging FilmsPaper OverwrapZipper BagInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ExxonMobil method |
| Melt Flow | 3.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Slip Level | 400 ppm | 400 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.3 MPa | 1500 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.3 MPa | 1500 psi | ASTM D882 |
| Film Elongation at Break, MD | 610 % | 610 % | ASTM D882 |
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 |
| Puncture Energy | 1.58 J | 1.17 ft-lb | ExxonMobil Method |
| Elmendorf Tear Strength MD | 20 g | 20 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 300 g | 300 g | ASTM D1922 |
| Dart Drop Test | <= 50.0 g | <= 0.110 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 44.8 MPa | 6500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 24.1 MPa | 3500 psi | ASTM D882 |
| 1% Secant Modulus, MD | 200 MPa | 29000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 214 MPa | 31000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | <= 253 °C | <= 487 °F | Peak Melting Point; ExxonMobil method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.1 % | 1.1 % | ASTM D1003 |
| Gloss | 92 % | 92 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Puncture Force | 7 lbf | ExxonMobil Method |