ExxonMobil LLDPE LL 1002YB Wire & Cable Linear Low Density Polyethylene Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer	Exxon Chemical
Trade Name	LLDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LLDPE LL 1002YB Wire & Cable Linear Low Density Polyethylene Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LL 1002YB is a C4 Ziegler Natta LLDPE for Low Voltage power cable and Telecom jacketing. The grade contains a higher level of antioxidants and has excellent Environmental Stress Crack Resistance (ESCR). Sufficient Carbon Black or UV Stabilizer should be added to meet jacketing specifications. Availability: Africa & Middle East, Asia Pacific, Europe, Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: YesApplications: Halogen-free flame retardant (HFFR) compoundsLV silane cross-linkable – 2 step processLV thermoplastic jacketingMV/HV thermoplastic jacketingTelecom thermoplastic jacketingInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.918 g/cc	0.0332 lb/in³	ExxonMobil method
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	48 @Time 15.0 sec	48 @Time 0.00417 hour	ASTM D2240
Tensile Strength at Break	17.2 MPa	2500 psi	ASTM D638
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
Elongation at Break	790 %	790 %	ASTM D638
Elongation at Yield	20 %	20 %	ASTM D638
Flexural Modulus, 1% Secant	255 MPa	37000 psi	ASTM D790

Thermal Properties	Metric	English	Comments
Melting Point	<= 248 °C	<= 478 °F	Peak Melting Point; ExxonMobil method

Electrical Properties	Metric	English	Comments
Volume Resistivity	5.00e+15 ohm-cm	5.00e+15 ohm-cm	ASTM D257
Dielectric Constant	2.2 @Frequency 60.0 Hz	2.2 @Frequency 60.0 Hz	ASTM D150
Dielectric Strength	55.1 kV/mm	1400 kV/in	500 V/sec; ASTM D149
Dissipation Factor	0.0010 @Frequency 60.0 Hz	0.0010 @Frequency 60.0 Hz	ASTM D150