ExxonMobil LL 8460.29 Rotational Molding Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade
Manufacturer Exxon Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LL 8460.29 Rotational Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LL 8460 is a linear low density hexene copolymer designed to offer excellent ESCR and toughness. This resin is ideally suited for applications that require the optimum balance of processability, stiffness and low temperature toughness. Availability: Latin America, North America and South America Additive: Stabilizer: YesLong Term UV-15 Applications: Agricultural TanksChemical Storage TanksLarge Size Playground EquipmentPalletsPotable Water TanksSeptic Tanks Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.938 g/cc
0.0339 lb/in³
ASTM D4883
ESCR 100% Igepal® >= 1000 hour
>= 1000 hour
ASTM D1693
ESCR 10% Igepal® 150 hour
150 hour
ASTM D1693
Melt Flow 3.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 17.93 MPa
2600 psi
2.0 in/min; ASTM D638
Elongation at Yield 20 %
20 %
2.0 in/min; ASTM D638
Flexural Modulus 0.758 GPa
110 ksi
1% secant; ASTM D790
Impact Test 94.9 J

@Thickness 3.17 mm,
Temperature -40.0 °C
70.0 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
ARM
258 J

@Thickness 6.35 mm,
Temperature -40.0 °C
190 ft-lb

@Thickness 0.250 in,
Temperature -40.0 °F
ARM
Thermal Properties Metric English Comments
Melting Point 127 °C
261 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 62.0 °C
144 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 39.0 °C
102 °F
ASTM D648