ExxonMobil LL 1235x70 Cast Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LL 1235x70 Cast Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LL 1235x70 is a butene LLDPE with improved stiffness. It can be used alone or as a component in packaging and industrial film.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ExxonMobil Method |
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238 |
| Slip Level | 400 ppm | 400 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 9.10 MPa | 1320 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.76 MPa | 1270 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 570 % | 570 % | ASTM D882 |
| Film Elongation at Break, TD | 780 % | 780 % | ASTM D882 |
| Puncture Energy | 1.36 J | 1.00 ft-lb | ExxonMobil |
| Elmendorf Tear Strength, MD | 0.984 g/micron | 25.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 9.350 g/micron | 237.5 g/mil | ASTM D1922 |
| Dart Drop | <= 2.46 g/micron | <= 62.5 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 45.8 MPa | 6640 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 24.3 MPa | 3520 psi | ASTM D882 |
| 1% Secant Modulus, MD | 166 MPa | 24100 psi | ASTM D882 |
| 1% Secant Modulus, TD | 172 MPa | 25000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 122 °C | 252 °F | Peak Melting Temperature; ExxonMobil Method |
| Crystallization Temperature | 110 °C | 230 °F | ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.4 % | 1.4 % | ASTM D1003 |
| Gloss | 90 % | 90 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8120 (473) (UF) Synthetic Oil
- Northstar Polymers MGB-A80AQ High Performance Polyurethane Cast Elastomer System 80A
- SABIC Innovative Plastics LNP THERMOCOMP QF008 PA6.10
- SABIC Innovative Plastics NORYL LEN2211 PPE+HIPS (Asia Pacific)
- A. Schulman POLYFORT™ FPP 4529 Mineral Filled Copolymer Polypropylene
- A. Schulman POLYBATCH™ Treated Pine 60181U/4 Concentrate Based In LLDPE
- Universal Wire Works BAg-2 (AMS 4768) Silver Brazing Filler Metal
- DuPont Performance Polymers VESPEL TP-8556 Polyimide
- Henkel Turco Aldet Cleaner
- DuPont Performance Polymers Zytel® HTN 51G50HSL BK083 Polyphthalamide (PPA)
Copyright © lookpolymers.com All Rights Reserved