Material Notes:

LL 1002.32 is a butene LLDPE resin designed for the cast film process. Films made from LL 1002.32 have very good tensile and toughness properties.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.918 g/cc	0.0332 lb/in³	ExxonMobil Method
Melt Flow	2.0 g/10 min	2.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	7.72 MPa	1120 psi	at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD	6.96 MPa	1010 psi	at 2% offset; ASTM D882
Film Elongation at Break, MD	450 %	450 %	ASTM D882
Film Elongation at Break, TD	850 %	850 %	ASTM D882
Puncture Energy	2.71 J	2.00 ft-lb	ExxonMobil
Elmendorf Tear Strength, MD	1.48 g/micron	37.5 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	17.22 g/micron	437.5 g/mil	ASTM D1922
Dart Drop	3.44 g/micron	87.5 g/mil	ASTM D1709
Film Tensile Strength at Break, MD	56.5 MPa	8190 psi	ASTM D882
Film Tensile Strength at Break, TD	28.8 MPa	4180 psi	ASTM D882
1% Secant Modulus, MD	109 MPa	15800 psi	ASTM D882
1% Secant Modulus, TD	125 MPa	18200 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	120 °C	248 °F	Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature	104 °C	219 °F	ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	1.6 %	1.6 %	ASTM D1003
Gloss	92 %	92 %	45°; ASTM D2457

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer