ExxonMobil LL 1001.32 Cast Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LL 1001.32 Cast Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LL 1001.32 is a butene LLDPE resin. Films made from LL 1001.32 have very good tensile and toughness properties.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil Method |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 7.93 MPa | 1150 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.24 MPa | 1050 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 |
| Film Elongation at Break, TD | 810 % | 810 % | ASTM D882 |
| Puncture Energy | 2.82 J | 2.08 ft-lb | ExxonMobil |
| Elmendorf Tear Strength, MD | 0.984 g/micron | 25.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 22.6 g/micron | 575 g/mil | ASTM D1922 |
| Dart Drop | 2.95 g/micron | 75.0 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 66.0 MPa | 9570 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.5 MPa | 4140 psi | ASTM D882 |
| 1% Secant Modulus, MD | 108 MPa | 15700 psi | ASTM D882 |
| 1% Secant Modulus, TD | 133 MPa | 19300 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 121 °C | 250 °F | Peak Melting Temperature; ExxonMobil Method |
| Crystallization Temperature | 106 °C | 223 °F | ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.7 % | 1.7 % | ASTM D1003 |
| Gloss | 90 % | 90 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- Omni Plastics OmniTech™ PA6 GR35 IM4 BK Flame Retardant
- SABIC Innovative Plastics GELOY XP4034 ASA+PC (Asia Pacific)
- Parker Chomerics CHO-SHIELD® 610 A/B Conductive Epoxy Paint
- Polimeri Europa SINKRAL B153/V4 ABS, Heat Stabilized, 17% Glass Fiber (discontinued **)
- SABIC Innovative Plastics Valox® IQ357 PBT+PC (Asia Pacific)
- Spartech E66091 General Purpose PVC
- Chesterton ARC NVE SYSTEM Vinyl Ester Lining
- Elektro-Isola G-Etronax PI Polyimide, Glass Fabric Reinforcement, Dark Brown, Sheets
- ExxonMobil ESCOREZ™ 2173 (Europe) Petroleum Hydrocarbon Resin
- Barlog Plastics KEBATER A0130 PBT/ABS, 30% glass fiber reinforced, low warpage
Copyright © lookpolymers.com All Rights Reserved