ExxonMobil LDPE LD 617.LN Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 617.LN Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 617.LN is a high flow, low density polyethylene homopolymer resin designed to provide excellent processability, flexibility and surface appearance. This multipurpose resin is performance engineered for applications such as housewares, overcaps and closures and concentrates.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoThermal Stabilizer: NoApplications: CapsClosuresCompoundingFood Packaging ContainersHouseware ArticlesInjection MoldingLabwareMasterbatch Base ResinInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.919 g/cc
0.0332 lb/in³
ExxonMobil method
Melt Flow 26 g/10 min

@Load 2.16 kg,
Temperature 190 °C
26 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 86

@Time 15.0 sec
86

@Time 0.00417 hour
ASTM D2240
Hardness, Shore D 42

@Time 15.0 sec
42

@Time 0.00417 hour
ASTM D2240
Tensile Strength at Break 7.58 MPa
1100 psi
ASTM D638
Tensile Strength, Yield 11.0 MPa
1600 psi
ASTM D638
Elongation at Break 120 %
120 %
ASTM D638
Elongation at Yield 30 %
30 %
ASTM D638
Flexural Modulus, 1% Secant 234 MPa
34000 psi
ASTM D790
Dart Drop, Total Energy 16.3 J

@Temperature 22.8 °C
12.0 ft-lb

@Temperature 73.0 °F
ASTM D3763
19.0 J

@Temperature -20.0 °C
14.0 ft-lb

@Temperature -4.00 °F
ASTM D3763
Thermal Properties Metric English Comments
Melting Point <= 230 °C
<= 446 °F
Peak Melting Point; ExxonMobil method
Vicat Softening Point 83.9 °C
183 °F
ASTM D1525