ExxonMobil LDPE LD 331.08 Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 331.08 Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 331.08 is a 5.9% vinyl acetate copolymer, higher clarity film resin. Film made from this resin exhibits superior impact strength and heat sealability.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: YesApplications: Coextrusion FilmsFoamsForm Fill and Seal PackagingFreezer FilmHigh Clarity FilmLamination FilmPoultry BagProduce BagsRice BagsInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.926 g/cc
0.0335 lb/in³
ExxonMobil method
Vinyl Acetate Content 2.9 %
2.9 %
ExxonMobil Method
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, TD 6.83 MPa
990 psi
ASTM D882
Film Elongation at Break, MD 360 %
360 %
ASTM D882
Film Elongation at Break, TD 650 %
650 %
ASTM D882
Puncture Energy 3.16 J
2.33 ft-lb
ExxonMobil Method
Elmendorf Tear Strength MD 140 g
140 g
ASTM D1922
Elmendorf Tear Strength TD 100 g
100 g
ASTM D1922
Dart Drop Test 170 g
0.375 lb
ASTM D1709A
Film Tensile Strength at Break, MD 6.89 MPa
1000 psi
ASTM D882
Film Tensile Strength at Break, TD 25.5 MPa
3700 psi
ASTM D882
1% Secant Modulus, MD 110 MPa
16000 psi
ASTM D882
1% Secant Modulus, TD 124 MPa
18000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 216 °C
<= 421 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 2.5 %
2.5 %
ASTM D1003
Gloss 84 %
84 %
45°; ASTM D2457
Descriptive Properties Value Comments
Puncture Force 14 lbf
ExxonMobil Method