ExxonMobil LDPE LD 150BW Wire & Cable Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 150BW Wire & Cable Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 150BW is a LDPE containing suitable for the production of LV and MV crosslinked insulation using the 1-step or 2-step silane technology. Through in-house compounding it can also be used in Medium Voltage peroxide cross-linkable insulation. Sufficient antioxidant and Cu-inhibitor should be added to meet specific ageing requirements.Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: YesApplications: LV Silane cross-linkable insulation – 1 step processMV/HV peroxide cross-linked insulationInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.923 g/cc
0.0333 lb/in³
ExxonMobil method
Melt Flow 0.75 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.75 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 50

@Time 15.0 sec
50

@Time 0.00417 hour
ASTM D2240
Tensile Strength at Break 13.8 MPa
2000 psi
ASTM D638
Tensile Strength, Yield 11.7 MPa
1700 psi
ASTM D638
Elongation at Break 580 %
580 %
ASTM D638
Elongation at Yield 20 %
20 %
ASTM D638
Flexural Modulus, 1% Secant 221 MPa
32000 psi
ASTM D790
Thermal Properties Metric English Comments
Melting Point <= 228 °C
<= 442 °F
Peak Melting Point; ExxonMobil method
Electrical Properties Metric English Comments
Volume Resistivity 6.00e+15 ohm-cm
6.00e+15 ohm-cm
ASTM D257
Dielectric Constant 2.1
2.1
ASTM D150
Dielectric Strength 51.2 kV/mm
1300 kV/in
ASTM D149
Dissipation Factor 0.00010
0.00010
ASTM D150