ExxonMobil LDPE LD 104BR Low Density Polyethylene Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Exxon Chemical
Trade Name	LDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LDPE LD 104BR Low Density Polyethylene Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 104BR is an LDPE grade, which offers good optical properties combined with increased stiffness.Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: 1000 ppmSlip: 750 ppmThermal Stabilizer: YesApplications: Blend PartnerBread BagsDisplay Packaging FilmFood packagingForm Fill and Seal PackagingFreezer FilmHigh Clarity FilmLamination FilmLight Duty Shrink Film Mail BagProduce BagsSalad BagsTextile PackagingInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.925 g/cc	0.0334 lb/in³	ExxonMobil method
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Antiblock Level	1000 ppm	1000 ppm
Slip Level	750 ppm	750 ppm

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	200 %	200 %	ASTM D882
Film Elongation at Break, TD	500 %	500 %	ASTM D882
Elmendorf Tear Strength MD	200 g	200 g	ASTM D1922
Elmendorf Tear Strength TD	120 g	120 g	ASTM D1922
Dart Drop Test	70.0 g	0.154 lb	ASTM D1709A
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
Film Tensile Strength at Break, TD	19.3 MPa	2800 psi	ASTM D882
1% Secant Modulus, MD	241 MPa	35000 psi	ASTM D882
1% Secant Modulus, TD	283 MPa	41000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 232 °C	<= 450 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	5.0 %	5.0 %	ASTM D1003
Gloss	68 %	68 %	45°; ASTM D2457