ExxonMobil LDPE LD 103.09 Low Density Polyethylene Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE |
| Manufacturer | Exxon Chemical |
| Trade Name | LDPE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LDPE LD 103.09 Low Density Polyethylene Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: LD 103 resins are homopolymer industrial film resins with excellent toughness. LD 103 resins have a low melt index, which provides good impact strength and melt strength over a range of gauges.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: YesApplications: Agricultural FilmBlend PartnerCo-Extrusion FilmsForm Fill and Seal PackagingFreezer FilmLinersMedium Duty Shrink FilmRubber Bale Wrap Information provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ExxonMobil method |
| Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.3 MPa | 1500 psi | ASTM D882 |
| Film Elongation at Break, MD | 150 % | 150 % | ASTM D882 |
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D882 |
| Puncture Energy | 1.08 J | 0.800 ft-lb | ExxonMobil Method |
| Elmendorf Tear Strength MD | 340 g | 340 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 70 g | 70 g | ASTM D1922 |
| Dart Drop Test | 140 g | 0.309 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4200 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 24.1 MPa | 3500 psi | ASTM D882 |
| 1% Secant Modulus, MD | 200 MPa | 29000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 255 MPa | 37000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | <= 226 °C | <= 439 °F | Peak Melting Point; ExxonMobil method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 11 % | 11 % | ASTM D1003 |
| Gloss | 50 % | 50 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Puncture Force | 10 lbf | ExxonMobil Method |