- ExxonMobil LDPE LD 071.LR Low Density Polyethylene Resin
ExxonMobil LDPE LD 071.LR Low Density Polyethylene Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE |
| Manufacturer | Exxon Chemical |
| Trade Name | LDPE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LDPE LD 071.LR Low Density Polyethylene Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: LD 071 Series case wrap film resins combine good processability with excellent strength and good film optics for bundling applications requiring proper shrink performance, toughness, burn-through resistance and clarity. Availability: Latin America, North America and South America Additive: Antiblock: 2000 ppmSlip: NoThermal Stabilizer: NoApplications:Blend PartnerCo-Extrusion FilmsCollation ShrinkConstruction FilmForm Fill and Seal PackagingFreezer FilmLamination FilmMedium Duty Shrink FilmPallet Shrink Film Information provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ExxonMobil method |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Antiblock Level | 2000 ppm | 2000 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.7 MPa | 1700 psi | ASTM D882 |
| Film Elongation at Break, MD | 130 % | 130 % | ASTM D882 |
| Film Elongation at Break, TD | 540 % | 540 % | ASTM D882 |
| Elmendorf Tear Strength MD | 510 g | 510 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 140 g | 140 g | ASTM D1922 |
| Dart Drop Test | 160 g | 0.353 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.1 MPa | 3200 psi | ASTM D882 |
| 1% Secant Modulus, MD | 234 MPa | 34000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 290 MPa | 42000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | <= 235 °C | <= 455 °F | Peak Melting Point; ExxonMobil method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 9.6 % | 9.6 % | ASTM D1003 |
| Gloss | 57 % | 57 % | 45°; ASTM D2457 |