ExxonMobil LD 313.NF Blown Film Resin

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 313.NF Blown Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LD 313.NF is a 3 wt% vinyl acetate copolymer. The vinyl acetate content of this resin provides good heat sealing and good cold temperature toughness when compared to LDPE homopolymers.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
ExxonMobil Method
Vinyl Acetate Content 3.0 %
3.0 %
ExxonMobil Method
Thickness 38.1 microns
1.50 mil
Melt Flow 2.5 g/10 min
2.5 g/10 min
ExxonMobil Method
Antiblock Level 2500 ppm
2500 ppm
Slip Level 800 ppm
800 ppm
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 230 %
230 %
ASTM D882
Film Elongation at Break, TD 580 %
580 %
ASTM D882
Elmendorf Tear Strength MD 240 g
240 g
ASTM D1922
Elmendorf Tear Strength TD 140 g
140 g
ASTM D1922
Elmendorf Tear Strength, MD 6.30 g/micron
160 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 3.674 g/micron
93.33 g/mil
ASTM D1922
Dart Drop 3.67 g/micron
93.3 g/mil
ASTM D1709
Dart Drop Test 140 g
0.309 lb
ASTM D1709
Film Tensile Strength at Break, MD 23.0 MPa
3330 psi
ASTM D882
Film Tensile Strength at Break, TD 20.8 MPa
3010 psi
ASTM D882
1% Secant Modulus, MD 164 MPa
23800 psi
ASTM D882
1% Secant Modulus, TD 188 MPa
27200 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 107 °C
225 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 5.7 %
5.7 %
ASTM D1003
Gloss 75 %
75 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer