ExxonMobil LD 141.87 Shrink Film Resin

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 141.87 Shrink Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LD 141.87 is a vinyl acetate copolymer film resin with very good toughness and shrink properties. Applications include Medium duty shrink wrap and Heavy duty bags.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.921 g/cc
0.0333 lb/in³
ExxonMobil Method
Vinyl Acetate Content 2.0 %
2.0 %
ExxonMobil Method
Melt Flow 0.30 g/10 min
0.30 g/10 min
ExxonMobil Method
Antiblock Level 6000 ppm
6000 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.96 MPa
1300 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 8.27 MPa
1200 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 200 %
200 %
ASTM D882
Film Elongation at Break, TD 500 %
500 %
ASTM D882
Elmendorf Tear Strength, MD 3.15 g/micron
80.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 6.30 g/micron
160 g/mil
ASTM D1922
Dart Drop 9.45 g/micron
240 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 22.1 MPa
3200 psi
ASTM D882
Film Tensile Strength at Break, TD 20.7 MPa
3000 psi
ASTM D882
1% Secant Modulus, MD 152 MPa
22000 psi
ASTM D882
1% Secant Modulus, TD 193 MPa
28000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 107 °C
225 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 20 %
20 %
ASTM D1003
Gloss 40 %
40 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer