ExxonMobil LD 135.09 Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 135.09 Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LD 135.09 is a homopolymer film resin with good clarity. Applications include food packaging, light to medium duty bags, and textile packaging.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.921 g/cc
0.0333 lb/in³
ExxonMobil Method
Thickness 38.1 microns
1.50 mil
Melt Flow 3.0 g/10 min
3.0 g/10 min
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.1 MPa
1460 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 10.3 MPa
1490 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 340 %
340 %
ASTM D882
Film Elongation at Break, TD 640 %
640 %
ASTM D882
Film Elongation at Yield, MD 6.2 %
6.2 %
ASTM D882
Film Elongation at Yield, TD 5.4 %
5.4 %
ASTM D882
Elmendorf Tear Strength MD 310 g
310 g
ASTM D1922
Elmendorf Tear Strength TD 180 g
180 g
ASTM D1922
Elmendorf Tear Strength, MD 8.134 g/micron
206.6 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 4.72 g/micron
120 g/mil
ASTM D1922
Dart Drop 2.62 g/micron
66.6 g/mil
ASTM D1709
Dart Drop Test 100 g
0.221 lb
ASTM D1709
Film Tensile Strength at Break, MD 26.3 MPa
3820 psi
ASTM D882
Film Tensile Strength at Break, TD 21.3 MPa
3090 psi
ASTM D882
1% Secant Modulus, MD 192 MPa
27800 psi
ASTM D882
1% Secant Modulus, TD 230 MPa
33400 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 109 °C
228 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 4.4 %
4.4 %
ASTM D1003
Gloss 80 %
80 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer