ExxonMobil LD 129.24 Cast Overwrap Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer	Exxon Chemical
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LD 129.24 Cast Overwrap Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 129.24 is a medium density homopolymer film resin with good clarity and excellent stiffness. Film made from LD 129.24 can be used in overwrap applications and in push-through type packaging equipment. LD 129.24 is suitable for processing in either blown or cast film equipment. Availability: Latin America, North America and South America Additive: Antiblock: 1000 ppmSlip: NoThermal Stabilizer: YesApplications: Bread BagsCast FilmCo-Extrusion FilmsDiaper BacksheetEmbossed FilmHygiene PackagingLabel FilmOverwrap FilmPaper Overwrap Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.929 g/cc	0.0336 lb/in³	ExxonMobil Method
Thickness	38.1 microns	1.50 mil
Melt Flow	2.3 g/10 min @Load 2.16 kg, Temperature 190 °C	2.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Antiblock Level	1000 ppm	1000 ppm

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	14.5 MPa	2100 psi	ASTM D882
Film Tensile Strength at Yield, TD	15.9 MPa	2300 psi	ASTM D882
Film Elongation at Break, MD	180 %	180 %	ASTM D882
Film Elongation at Break, TD	460 %	460 %	ASTM D882
Puncture Energy	0.316 J	0.233 ft-lb	ExxonMobil Method
Elmendorf Tear Strength MD	100 g	100 g	ASTM D1922
Elmendorf Tear Strength TD	270 g	270 g	ASTM D1922
Dart Drop Test	70.0 g	0.154 lb	ASTM D1709
Film Tensile Strength at Break, MD	23.6 MPa	3420 psi	ASTM D882
Film Tensile Strength at Break, TD	18.6 MPa	2700 psi	ASTM D882
1% Secant Modulus, MD	324 MPa	47000 psi	ASTM D882
1% Secant Modulus, TD	386 MPa	56000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	117 °C	242 °F	Peak Melting Temperature; ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	8.1 %	8.1 %	ASTM D1003
Gloss	68 %	68 %	45°; ASTM D2457

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer