ExxonMobil LD 102.LC Thin Gauged Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LD 102.LC Thin Gauged Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
L Product Description: LD 102.LC is a formulated homopolymer, garment film resin with good toughness. It is capable of being drawndown to thing gauges.Availability: Latin America, North America and South America Additive: Antiblock: 3000 ppmSlip: 1200 ppmProcessing Aid: No Thermal Stabilizer: YesApplications: Blown FilmCast FilmCompoundingGarment FilmLaundry Film Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ExxonMobil Method |
| Melt Flow | 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Antiblock Level | 3000 ppm | 3000 ppm | |
| Slip Level | 1200 ppm | 1200 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 9.65 MPa | 1400 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.3 MPa | 1500 psi | ASTM D882 |
| Film Elongation at Break, MD | 210 % | 210 % | ASTM D882 |
| Film Elongation at Break, TD | 520 % | 520 % | ASTM D882 |
| Puncture Energy | 0.203 J | 0.150 ft-lb | ExxonMobil Method |
| Elmendorf Tear Strength MD | 530 g | 530 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 200 g | 200 g | ASTM D1922 |
| Dart Drop Test | 60.0 g | 0.132 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 17.9 MPa | 2600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | ASTM D882 |
| 1% Secant Modulus, MD | 179 MPa | 26000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 207 MPa | 30000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 110 °C | 230 °F | Peak Melting Temperature; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.8 % | 7.8 % | ASTM D1003 |
| Gloss | 69 % | 69 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |