ExxonMobil LD 102.74 Thin Gauged Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LD 102.74 Thin Gauged Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LD 102 series are homopolymer, good clarity, laundry and dry cleaning film resins capable of providing a tough film in very thin gaugesInformation provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ExxonMobil Method |
| Melt Flow | 6.8 g/10 min | 6.8 g/10 min | ExxonMobil Method |
| Antiblock Level | 24000 ppm | 24000 ppm | |
| Slip Level | 1350 ppm | 1350 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 8.96 MPa | 1300 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.65 MPa | 1400 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 380 % | 380 % | ASTM D882 |
| Film Elongation at Break, TD | 610 % | 610 % | ASTM D882 |
| Film Elongation at Yield, MD | 7.0 % | 7.0 % | ASTM D882 |
| Film Elongation at Yield, TD | 7.4 % | 7.4 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 5.12 g/micron | 130 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.31 g/micron | 84.0 g/mil | ASTM D1922 |
| Dart Drop | 2.60 g/micron | 66.0 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 20.0 MPa | 2900 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | ASTM D882 |
| 1% Secant Modulus, MD | 157 MPa | 22800 psi | ASTM D882 |
| 1% Secant Modulus, TD | 182 MPa | 26400 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 110 °C | 230 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 87.2 - 91.1 °C | 189 - 196 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 83 % | 83 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Formed and Deep Draw Quality
- LG Chemical 501S-S HIPS
- Styrolution PS 1600 GPPS
- A. Schulman POLYTROPE™ TPP 503 Injection Molding Grade Olefinic Thermoplastic Elastomer
- Polyram PlusTek PA108 Nylon6/6.6 Alloy for Injection Molding
- Covestro Makrolon® 2800 Polycarbonate
- Eurotec® Tecopet® PT70 GR30 NL100 MB PET, 30% glass fiber reinforced, impact modified, heat stabilized, natural
- Arlon 51576XC15A 0.015" Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Bulk Molding Compounds BMC A50-EG Low Glass, Encapsulation Grade Molding Compound
- Solvay Specialty Polymers Algoflon® L101-1 Polytetrafluoroethylene (PTFE) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved