ExxonMobil Exxtral™ BNU 013 Performance Polyolefin

Category	Polymer , Thermoplastic , Ethylene Butyl Acrylate
Manufacturer	Exxon Chemical
Trade Name	Exxtral™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Exxtral™ BNU 013 Performance Polyolefin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A specialty thermoplastic polyolefin resin characterized by a good impact resistance, high stiffness, good scratch and good surface finishing designed for automotive interior applications such as door panels.Availability: Africa & Middle East, Asia Pacific, Europe, Latin America, South America and North America Features: Balanced Stiffness/ToughnessGood Impact ResistanceGood ProcessabilityHigh Scratch ResistanceHigh StiffnessMedium Flow Uses: Automotive ApplicationsAutomotive Interior PartsAutomotive Interior Trim Processing Method: Injection MoldingInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.900 g/cc	0.0325 lb/in³	ISO 1183
Melt Flow	16 g/10 min @Load 2.16 kg, Temperature 230 °C	16 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	13.0 MPa	1890 psi	ISO 527-2
Tensile Strength, Yield	17.0 MPa	2470 psi	ISO 527-2
Elongation at Yield	4.0 %	4.0 %	ISO 527-2
Tensile Modulus	1.01 GPa	146 ksi	Secant; ISO 527-2
Flexural Modulus	1.03 GPa	149 ksi	ISO 178
Charpy Impact, Notched	0.903 J/cm² @Temperature -20.0 °C	4.30 ft-lb/in² @Temperature -4.00 °F	Complete Break; ISO 179
	1.30 J/cm² @Temperature 0.000 °C	6.20 ft-lb/in² @Temperature 32.0 °F	Complete Break; ISO 179
	2.10 J/cm² @Temperature 22.8 °C	10.0 ft-lb/in² @Temperature 73.0 °F	Complete Break; ISO 179

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	68.9 °C	156 °F	ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi)	45.0 °C	113 °F	ISO 75-2/A