Material Notes:
Product Description: Exceed 3527PA is a metallocene ethylene-hexene copolymer. Films made from Exceed 3527PA have high modulus and outstanding tensile, impact and puncture resistance properties. These superior properties together with excellent drawability make this a versatile polymer for mono layer and multi layer cast stretch film applications. Availability: Latin America, North America and South AmericaAdditive:Antiblock: NoSlip: NoProcessing Aid: YesThermal Stabilizer: YesApplications: Artificial grassCast FilmCast Stretch FilmDiaper BacksheetHygiene FilmOverwrap FilmPersonal Care Information provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.927 g/cc
0.0335 lb/in³
ExxonMobil method
Melt Flow 3.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.3 MPa
1500 psi
ASTM D882
Film Tensile Strength at Yield, TD 9.65 MPa
1400 psi
ASTM D882
Film Elongation at Break, MD 530 %
530 %
ASTM D882
Film Elongation at Break, TD 750 %
750 %
ASTM D882
Puncture Energy 2.60 J
1.92 ft-lb
ExxonMobil Method
Elmendorf Tear Strength MD 70 g
70 g
ASTM D1922
Elmendorf Tear Strength TD 400 g
400 g
ASTM D1922
Dart Drop Test 60.0 g
0.132 lb
ASTM D1709
Film Tensile Strength at Break, MD 61.4 MPa
8900 psi
ASTM D882
Film Tensile Strength at Break, TD 40.7 MPa
5900 psi
ASTM D882
1% Secant Modulus, MD 186 MPa
27000 psi
ASTM D882
1% Secant Modulus, TD 207 MPa
30000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 250 °C
<= 482 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 2.8 %
2.8 %
ASTM D1003
Gloss 87 %
87 %
45°; ASTM D2457
Descriptive Properties Value Comments
Puncture Force 10 lbf
ExxonMobil Method