ExxonMobil Exceed™ 3527PA Metallocene Polyethylene Resin (European Grade)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Exxon Chemical
Trade Name Exceed™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Exceed™ 3527PA Metallocene Polyethylene Resin (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Exceed 3527PA is a metallocene ethylene-hexene copolymer. Films made of Exceed 3527PA have high modulus and outstanding tensile, impact and puncture resistance properties. These superior properties together with excellent drawability make this a versatile polymer for mono layer and multi layer cast film applications.Availability: Africa & Middle East and EuropeAdditive:Antiblock: NoSlip: No Applications:Artificial grassCast FilmCast Stretch FilmDiaper Backsheet Hygiene FilmOverwrap FilmPersonal Care Information provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.927 g/cc
0.0335 lb/in³
ExxonMobil method
Melt Flow 3.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 580 %
580 %
ASTM D882
Film Elongation at Break, TD 780 %
780 %
ASTM D882
Elmendorf Tear Strength MD 100 g
100 g
ASTM D1922
Elmendorf Tear Strength TD 360 g
360 g
ASTM D1922
Dart Drop Test 90.0 g
0.198 lb
ASTM D1709
Film Tensile Strength at Break, MD 68.9 MPa
10000 psi
ASTM D882
Film Tensile Strength at Break, TD 75.8 MPa
11000 psi
ASTM D882
1% Secant Modulus, MD 179 MPa
26000 psi
ASTM D882
1% Secant Modulus, TD 200 MPa
29000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 350 °C
<= 662 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 2.4 %
2.4 %
ASTM D1003
Gloss 14 %
14 %
45°; ASTM D2457
Descriptive Properties Value Comments
Puncture Force 14 lbf
ExxonMobil Method