ExxonMobil Exceed™ 2018CA Metallocene Polyethylene Resin (European Grade)

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	Exxon Chemical
Trade Name	Exceed™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Exceed™ 2018CA Metallocene Polyethylene Resin (European Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Exceed 2018CA is a metallocene ethylene-hexene copolymer. The higher melt index makes this polymer ideally suited for blending into LDPE rich films as well as skin layer in coextrusion applications. Availability: Africa & Middle East and EuropeAdditive:Antiblock: NoSlip: No Processing Aid: Yes Thermal Stabilizer: Yes Applications: Agricultural FilmBlown Film Blown Stretch FilmBread BagsCast FilmCast Stretch Film Food packagingFreezer FilmGeneral Packaging Heavy Duty Bags Hygiene filmLamination FilmMulch FilmMultilayer Packaging FilmPackaging Films Information provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.918 g/cc	0.0332 lb/in³	ExxonMobil method
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	600 %	600 %	ASTM D882
Film Elongation at Break, TD	730 %	730 %	ASTM D882
Elmendorf Tear Strength MD	300 g	300 g	ASTM D1922
Elmendorf Tear Strength TD	400 g	400 g	ASTM D1922
Dart Drop Test	1400 g	3.09 lb	ASTM D1709
Film Tensile Strength at Break, MD	75.8 MPa	11000 psi	ASTM D882
Film Tensile Strength at Break, TD	64.8 MPa	9400 psi	ASTM D882
1% Secant Modulus, MD	172 MPa	25000 psi	ASTM D882
1% Secant Modulus, TD	179 MPa	26000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 244 °C	<= 471 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	3.0 %	3.0 %	ASTM D1003
Gloss	13 %	13 %	45°; ASTM D2457

Descriptive Properties	Value	Comments
Puncture Force	22 lbf	ExxonMobil Method