ExxonMobil Exceed™ 2018CA Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Blow Molding Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Exceed™ 2018CA Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Exceed 2018CA resin is an ethylene based polymer produced with metallocene single site catalysts using ExxonMobil Chemicals EXXPOL® Technology. The higher melt index makes this polymer ideally suited for blending into LDPE rich films as well as skin layer in coextrusion applications.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ExxonMobil Method
Thickness 25.4 microns
1.00 mil
Melt Flow 2.0 g/10 min
2.0 g/10 min
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 600 %
600 %
ASTM D882
Film Elongation at Break, TD 730 %
730 %
ASTM D882
Elmendorf Tear Strength, MD 12.0 g/micron
305 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 16.0 g/micron
406 g/mil
ASTM D1922
Dart Drop 55.00 g/micron
1397 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 75.8 MPa
11000 psi
ASTM D882
Film Tensile Strength at Break, TD 65.5 MPa
9500 psi
ASTM D882
1% Secant Modulus, MD 169 MPa
24500 psi
ASTM D882
1% Secant Modulus, TD 179 MPa
26000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 118 °C
244 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 3.0 %
3.0 %
ASTM D1003
Gloss 13 %
13 %
60° angle; ASTM D2457
Descriptive Properties Value Comments
Features PPA and Thermal Stabilizer