ExxonMobil Exceed™ 1518EC Tough Premium Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Blow Molding Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Exceed™ 1518EC Tough Premium Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Exceed 1518EC resin is a hexene copolymer produced using ExxonMobil Chemicals EXXPOL® Technology. Films made from 1518EC resin have outstanding tensile, impact strength and puncture. These superior strength properties, along with excellent drawability, allow downguaging.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ExxonMobil Method
Thickness 25.4 microns
1.00 mil
Melt Flow 1.5 g/10 min
1.5 g/10 min
ExxonMobil Method
Antiblock Level 5000 ppm
5000 ppm
Slip Level 800 ppm
800 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.96 MPa
1300 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 8.96 MPa
1300 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 500 %
500 %
ASTM D882
Film Elongation at Break, TD 570 %
570 %
ASTM D882
Puncture Energy 1.59 J
1.17 ft-lb
Exxon Mobil Method
Elmendorf Tear Strength, MD 12.6 g/micron
320 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 18.5 g/micron
470 g/mil
ASTM D1922
Dart Drop 21.3 g/micron
540 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 39.3 MPa
5700 psi
ASTM D882
Film Tensile Strength at Break, TD 32.4 MPa
4700 psi
ASTM D882
1% Secant Modulus, MD 179 MPa
26000 psi
ASTM D882
1% Secant Modulus, TD 185 MPa
26900 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 119 °C
246 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 21 %
21 %
ASTM D1003
Gloss 36 %
36 %
45°, MD; ASTM D2457
40 %
40 %
45°, TD; ASTM D2457
Descriptive Properties Value Comments
Features PPA and Thermal Stabilizer